The invention discloses an aqueous etching ink, which is prepared by mixing water polyurethane emulsion, water epoxy resin emulsion, mixed acid, kaolin, bentonite, talc powder, defoaming agent and leveling agent. The aqueous etching ink of the invention is mixed and used with a polyurethane emulsion and an epoxy resin emulsion, so that the ink line is still clear and full, and the printing performance does not decrease with the passage of time. The use of mixed acid collocation ink can be fully etched touch screen conductive composition in ITO material; water soluble ink and stripping out of good performance, easy to clean and remove; screen printing line image resolution is better than the commercially available aqueous etching ink.
【技术实现步骤摘要】
一种水性蚀刻油墨
本专利技术涉及油墨领域,具体涉及一种水性蚀刻油墨。
技术介绍
蚀刻油墨主要采用强酸和中强酸作为蚀刻剂,可保证ITO能被彻底蚀刻,不会造成短路等不良现象。使用水性蚀刻油墨,突破了传统工艺必须使用保护油墨的惯性思维,在蚀刻过程中无需使用保护油墨,简化了蚀刻工艺,减少原材料消耗,无挥发性有机物,最大限度减少废酸废碱液的排放,提高产品质量。水性蚀刻油墨由蚀刻剂、联结料、填充料以及助剂组成。其优点之处在于:水性联结料分子量低、黏度低、水溶性好、耐酸性强;附着力低,水溶性强,易清洗剥落,保水性能好,耐酸稳定性好;蚀刻工艺简化,减少了对环境造成的危害,为企业带来巨大的经济效益并可实现产业升级。
技术实现思路
本专利技术目的在于,提供一种水性蚀刻油墨,本专利技术采用的技术方案如下:一种水性蚀刻油墨,其特征在于,由以下组分按重量百分比混合制备而成:水性聚氨酯乳液20-40份水性环氧树脂乳液10-30份混合酸2-10份高岭土10-20份膨润土10-20份滑石粉10-20份消泡剂0.1-1份流平剂0.1-1份。优选地,所述的混合酸是由2份磷酸,2份硫酸,1份对甲苯磺酸混合组成。优选地,所述混合酸的浓度为40-60%。优选地,所述的消泡剂是聚硅氧烷—聚醚共聚乳液型消泡剂。优选地,所述的高岭土,膨润土,滑石粉的粒径在1000-1500目。本专利技术相对于现有技术的有益效果是:本专利技术的水性蚀刻油墨,使用聚氨酯乳液与环氧树脂乳液混合搭配使用,使得油墨线路依然清晰饱满,印刷性能不会随时间的推移而降低。混合酸搭配使用油墨可完全蚀刻触摸屏ITO材料中的导电成分;油墨水溶性以 ...
【技术保护点】
一种水性蚀刻油墨,其特征在于,由以下组分按重量百分比混合制备而成:水性聚氨酯乳液 20‑40份水性环氧树脂乳液 10‑30份混合酸 2‑10份高岭土 10‑20份膨润土 10‑20份滑石粉 10‑20份消泡剂 0.1‑1份流平剂 0.1‑1份。
【技术特征摘要】
1.一种水性蚀刻油墨,其特征在于,由以下组分按重量百分比混合制备而成:水性聚氨酯乳液20-40份水性环氧树脂乳液10-30份混合酸2-10份高岭土10-20份膨润土10-20份滑石粉10-20份消泡剂0.1-1份流平剂0.1-1份。2.根据权利要求1所述的水性蚀刻油墨,其特征在于,所述的混合酸是由2份磷酸,2份硫...