The invention discloses a PVC water-based gravure ink, industrial printing ink, gravure printing ink raw materials according to the following: 516 the mass fraction ratio of waterborne PU resin 50%, water paste 35%, alcohol 13%, attapulgite and bentonite, 0.1% 0.7%, 810 0.1%, 245 defoamer wetting agent 0.2%, wetting agent 420 0.1%, 241, 0.5%, 935 thickener thickener, water 2%. In the premise of favorable environment protection and safety, the invention effectively solves the drying property of a water-based plastic film gravure ink, the fastness to rubbing, the phenomenon of sticking back and the water resistance.
【技术实现步骤摘要】
PVC水性凹印墨
本专利技术涉及工业印墨
,具体地说,是PVC水性凹印墨。
技术介绍
长期以来,印刷、印墨制备行业,包括广大民众均将印刷用墨称之为“油墨”。这是因为传统印刷用墨中材料大多数是石油的附属品,具有极强的亲油疏水特性。传统油墨由树脂、色料、溶剂和助剂四个部分组配制备而成。其中“溶剂”占的比重很大,溶剂是用来溶解物质的,从而在化解树脂,研磨色浆,生产助剂和调整印墨粘度的各环节上均需使用溶剂。所以传统的油墨行业内也称之为“溶剂墨”,在凹版印墨中其溶剂所占比率均大于60%,且在印刷过程中还得加入大量的溶剂对印墨反复稀释。
技术实现思路
本专利技术的目的在于克服现有技术的不足,提供PVC水性凹印墨。本专利技术涉及PVC水性凹印墨,所述凹印墨的原料按以下质量分数配比:516水性PU树脂50%、水性色浆35%、酒精13%、棒土0.1%、膨润土0.7%、810消泡剂0.1%、245润湿剂0.2%、420润湿剂0.1%、241增稠剂0.5%、935增稠剂2%、水。与现有技术相比,本专利技术的积极效果是:本专利技术在有利环保,确保安全的前提下,有效地解决了全水基塑料膜凹版印墨的干燥性能,揉搓牢度,回粘现象及抗水性的问题。具体实施方式本专利技术提供PVC水性凹印墨,为使本专利技术的目的、技术方案及效果更佳清楚、明确,下面对本专利技术进一步详细说明。应当理解,此处所描述的具体实施例仅用以解释本专利技术,并不用与限定本专利技术。PVC水性凹印墨,其特征在于,所述凹印墨的原料按以下质量分数配比:516水性PU树脂50%、水性色浆35%、酒精13%、棒土0.1%、膨润土0 ...
【技术保护点】
PVC水性凹印墨,其特征在于,所述凹印墨的原料按以下质量分数配比:516水性PU树脂50%、水性色浆35%、酒精13%、棒土0.1%、膨润土0.7%、810消泡剂0.1%、245润湿剂0.2%、420润湿剂0.1%、241增稠剂0.5%、935增稠剂2%、水。
【技术特征摘要】
1.PVC水性凹印墨,其特征在于,所述凹印墨的原料按以下质量分数配比:516水性PU树脂50%、水性色浆35%、酒精13%、棒土0....
【专利技术属性】
技术研发人员:朱思海,
申请(专利权)人:天津市虹化染料化工有限公司,
类型:发明
国别省市:天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。