The invention provides a preparation of gypsum gypsum slag fried dry mixed mortar method, the direct use of hot slag gangue power plant discharged slag machine in fried mixed frying desulfurization gypsum, and then mix the refined plastic ball mill, sieving made of gypsum powder and slag sand, adding additives by mixing ingredients made of gypsum powder mortar. The method of the invention uses hot slag waste heat frying desulfurization gypsum, separate calcining desulfurization gypsum is saved, save energy and calcining equipment investment, simple production process, low preparation cost, for the power plant desulfurization gypsum slag and opens up a new way of efficient resource utilization, environmental protection, to achieve the dual effect the utilization of waste.
【技术实现步骤摘要】
本专利技术属于工业固体废弃物资源化再生利用
，具体涉及一种渣炒石膏制备石膏干混砂浆的方法。
技术介绍
我国循环流化床煤矸石发电技术已达到国际先进水平，煤矸石等低热值煤发电装机已达约3000万kW，加入在建机组总装机规模约达3500万kW，煤矸石年利用量达2亿多吨，为国家节能减排作出巨大贡献。而与此同时，矸石电厂会排放大量的脱硫石膏与炉渣，难以利用，造成矸石电厂能源和资源浪费。矸石电厂脱硫石膏经炒制加工可用于石膏制品和建筑石膏，但脱硫石膏炒制需经烘干、脱水等工序，能耗高、热转化效率低，吨石膏粉的炒制成本约80元。矸石电厂排放的炉渣，出炉温度约700℃，炉渣粒径小于8mm，排放炉渣的基本物理性能指标均满足轻集料要求，经细化整形后可制成轻集料砂。石膏干混砂浆具有优越的粘结性，防火耐火性能，以及良好的呼吸性，是一种新型的绿色、健康、环保的墙体抹灰建筑材料。而现有的石膏干混砂浆是以石膏粉与砂为主要原料，加入1～2％的助剂配制而成，砂膏比约为2.5:1，其中砂为中细砂，目前通常采用天然砂，使用前需烘干处理，现有的这种石膏干混砂浆制备成本高。
技术实现思路
本专利技术的目的...
【技术保护点】
一种渣炒石膏制备石膏干混砂浆的方法，其特征在于：包括如下步骤：1)将循环流化床锅炉排出的热炉渣与脱硫石膏送入渣炒机混合，使脱硫石膏转变为半水石膏；2)将从渣炒机中排出的混合料经球磨机细化整形；3)将从球磨机排出的混合料筛分成石膏粉、炉渣砂和弃渣；4)取步骤3)得到的石膏粉与炉渣砂作原料，加入助剂，经配料混合均匀，即得到石膏干混砂浆。
【技术特征摘要】
1.一种渣炒石膏制备石膏干混砂浆的方法，其特征在于：包括如下步骤：1)将循环流化床锅炉排出的热炉渣与脱硫石膏送入渣炒机混合，使脱硫石膏转变为半水石膏；2)将从渣炒机中排出的混合料经球磨机细化整形；3)将从球磨机排出的混合料筛分成石膏粉、炉渣砂和弃渣；4)取步骤3)得到的石膏粉与炉渣砂作原料，加入助剂，经配料混合均匀，即得到石膏干混砂浆。2.如权利要求1所述的渣炒石膏制备石膏干混砂浆的方法，其特征在于：所述步骤1)中热炉渣与脱硫石膏混合前热炉渣的温度不低于500℃。3.如权利要求1所述的渣炒石膏制备石膏干混砂浆的方法，其特征在于：所述步骤1)中热炉渣与脱硫石膏的质量比为1:1～1:2。4.如权利要求1所述的渣炒石膏制备石膏干混砂浆的方法，其特征在于：所述步骤2)渣炒机中排出的混合料温度不低于130℃。5.如权利...