A heat-resistant friction material, containing the component and component parts by weight are as follows: study fiber of 25 to 35; 15 to 20 portions of cryolite; magnetite powder 30 ~ 35; antimony 3 ~ 6; 8 to 15 portions of adhesive. The preparation method comprises the following steps: S01, ingredients according to the components and the weight of a material containing; S02, the raw materials are mixed evenly, put into smelting equipment for smelting the raw materials melting and plasticizing; S03, plasticized materials after crushing into granular. The invention has the advantages that the recession performance of thermal recession friction materials in a certain proportion of the incorporation of the friction plate can improve the friction heat, friction coefficient increases friction at high temperature, to ensure the stability of the vehicle brake temperature.
【技术实现步骤摘要】
本专利技术涉及一种摩擦材料及其制备
，特别是一种掺入汽车刹车片的摩擦片中的抗热衰退摩擦材料及其制备方法。
技术介绍
刹车片是汽车刹车系统中最关键的安全零件，对汽车制动性能的好坏起决定性作用。刹车片一般由钢板、粘接隔热层和摩擦片构成，刹车时摩擦片被挤压在刹车盘上产生摩擦，从而达到车辆减速刹车的目的。现有的摩擦片均存在热衰退的现象，热衰退就是人们常说的刹车热衰减，是由于刹车片长时间在高负荷状态下工作或者是在连续刹车的情况下，摩擦片温度迅速上升，摩擦力矩显著下降引起的，表现为制动力不足以致刹车距离变长，影响高温制动的稳定性。
技术实现思路
本专利技术的目的是克服现有技术的不足，而提供一种抗热衰退摩擦材料及其制备方法，改善了现有的摩擦片的热衰退性能。本专利技术的技术方案是：一种抗热衰退摩擦材料，含有的组份及各组份的重量份数如下：纳凯夫纤维25～35份；冰晶石15～20份；磁铁矿粉30～35份；硫化锑3～6份；胶黏剂8～15份。本专利技术进一步的技术方案是:含有的组份还包括硫酸钡，重量份数为15～20份。<...
【技术保护点】
一种抗热衰退摩擦材料，其特征是，含有的组份及各组份的重量份数如下：纳凯夫纤维25～35份；冰晶石15～20份；磁铁矿粉30～35份；硫化锑3～6份；胶黏剂8～15份。
【技术特征摘要】
1.一种抗热衰退摩擦材料，其特征是，含有的组份及各组份的重量份数如下：纳凯夫纤维25～35份；冰晶石15～20份；磁铁矿粉30～35份；硫化锑3～6份；胶黏剂8～15份。
2.如权利要求1所述的抗热衰退摩擦材料，其特征是，含有的组份还包括硫酸钡，重量份数为15～20份。
3.如权利要求2所述的抗热衰退摩擦材料，其特征是，含有的组份及各组份的重量份数如下，纳凯夫纤维35份；冰晶石15份；磁铁矿粉30份；硫化锑3份；胶黏剂8份；硫酸钡15份。
4.如权利要求2所述的抗热衰退摩擦材料，其特征是，含有的组份及各组份的重量份数如下，纳凯夫纤维35份；冰晶石15份；磁铁矿粉30份；硫化锑3份；胶黏剂15份；硫酸钡20...
【专利技术属性】
技术研发人员：于海泉，郑辉，林凌，
申请(专利权)人：衡阳市安骋汽车配件有限公司，
类型：发明
国别省市：湖南;43