High temperature hard glaze formula for bone porcelain and process for producing bone porcelain. Guzhici recipe of high temperature hard glaze material components are quartz, feldspar, talc, porcelain powder, calcium carbonate, dolomite, kaolinite and frit; production process for bonechina: the first step is in the blank after drying the front spraying high temperature hard bone porcelain glaze, at the same time in the body surface by copying sagger support, to prevent the body deformation, and then into the kiln inner element 1270 to 1280 DEG C. firing; the second step is firing at the first high temperature glaze spraying hard porcelain products back into the low temperature spraying glaze, glaze firing within 1050 to 1160 DEG C. second glaze. The bone porcelain product produced by the present invention has high glaze hardness, high strength of porcelain piece, good thermal stability, no deformation and no lead content. The invention is suitable for producing various daily-use ceramic products.
【技术实现步骤摘要】
本专利技术属于化工陶瓷材料
，特别是骨质瓷用高温硬质釉配方及骨质瓷生产工艺。
技术介绍
现有的骨质瓷一般都是采用高铅釉，一次施釉，一次釉烧的工艺烧成，生产出的产品含铅量高，对人的身体有害，而且陶瓷产品的釉面硬度差，瓷件强度低，热稳定性差，产品易变形。由于产品的铅溶出量超标，使得日用陶瓷产品出口受到很大限制。
技术实现思路
本专利技术的目的是针对上述现有骨质瓷产品存在的不足，提供一种解决骨质瓷用釉铅超标，提高骨质瓷釉面硬度和瓷件的强度，改善骨质瓷的热稳定性差，解决骨质瓷易变形问题的骨质瓷用高温硬质釉配方及骨质瓷生产工艺。本专利技术的任务是以如下方式完成的骨质瓷用高温硬质釉配方的材料组份重量百分比最大范围是石英15---30％，长石30---50％，滑石3---10％，瓷粉5---25％，碳酸钙5---15％，白云石3---10％，高嶺土3---10％，熔块3---8％；较佳范围是石英15---25％，长石35---45％，滑石3---8％，瓷粉5---10％，碳酸钙10---15％，白云石4---9％，高嶺土3---8％，熔块3---6％；最佳范围是石英15％，...
【技术保护点】
一种骨质瓷用高温硬质釉配方及骨质瓷生产工艺，其特征在于骨质瓷用高温硬质釉配方的材料组份是石英、长石、滑石、瓷粉、碳酸钙、白云石、高嶺土和熔块；骨质瓷生产工艺为：第一步是在干燥后的坯体的正面喷施骨质瓷用高温硬质釉，同时在坯体背面用仿形匣钵支撑，然后送入素窑内在１２７０Ｃ－－１２８０Ｃ烧成；第二步是在第一次喷施高温硬质釉烧成的瓷件制品的背面喷施低温釉，送入釉烧窑内在１０５０Ｃ－－－１１６０Ｃ进行第二次釉烧。
【技术特征摘要】
【专利技术属性】
技术研发人员：赵孟冬，李素芬，李连明，赵学仁，赵楠，李尹，
申请(专利权)人：赵孟冬，
类型：发明
国别省市：13[中国|河北]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。