粉煤灰全高钛重矿渣泵送混凝土制造技术

本发明专利技术公开了一种粉煤灰全高钛重矿渣泵送混凝土，该混凝土按标准ＪＧＪ５５设计配合比，以高钛重矿渣砂、渣石为混凝土粗细集料，再掺入粉煤灰、水泥、外加剂和水混合配制而成，粉煤灰用量视水泥用量而定，为水泥用量的１０～４０％，计算高钛重矿渣砂和高钛重矿渣碎石用量的砂率为３５～４５％，外加剂可选用萘系、氨基磺酸盐系及丙羧酸等多种具有减水作用的外加剂，该混凝土强度高，实现了高炉渣的再利用。

Fly ash full high titanium heavy slag pumping concrete

The invention discloses a fly ash heavy high titanium slag concrete, the concrete mix design according to the standard of JGJ55, with high titanium heavy slag sand, slag concrete as coarse aggregates, then mixed with fly ash, cement, admixture and water mixed together, the amount of fly ash as cement dosage set the amount of cement is 10 ~ 40%, the calculation of high titanium heavy slag sand and high titanium heavy slag gravel sand content rate was 35 ~ 45%, the admixture can be used naphthalene, sulfamate and propylene carboxylic acid and other with water reducing admixture, the concrete strength is high, then the use of blast furnace slag the.

【技术实现步骤摘要】

本专利技术属建材
，涉及一种混凝土，特别涉及一种粉煤灰全高钛重矿渣泵送混凝土。
技术介绍
混凝土是现代工程结构的主要材料，我国每年混凝土用量约10亿m3，居世界首位，随着我国施工技术的不断提高以及越来越多城市对施工过程的环境要求，许多土建工程已经广泛使用泵送混凝土。武钢、首钢等单位自60年代起就着手高炉渣的研究与利用，攀钢于20世纪70年代末相继开展了高炉渣综合利用的研究，并结合攀钢高炉渣钛含量高的特点颁布了DB/5104Q13001-88《混凝土用高钛重矿渣碎石技术条件》标准。2004年以来，攀钢开展了对高钛型高炉渣做混凝土集料的深入研究，并颁布了相应的高钛重矿渣砂、高钛重矿渣碎石标准以及高钛重矿渣混凝土施工技术规程。规程对高钛重矿渣砂石的生产、使用做出了严格的规定。现有技术中的粉煤灰全矿渣混凝土(公告号CN1080625A，申请号92104810.6)使用的骨料是普通高炉渣，不是本专利技术所说的高钛重矿渣。两者材料组成和性能有差距。由于普通高炉渣含钛量低，实验证明，在配制混凝土时，其稳定性差，且由于其松散容重(1300--1350kg/m3)低，所以不利于配制高品级高强本文档来自技高网...

【技术保护点】
粉煤灰全高钛重矿渣泵送混凝土，其组分包括粉煤灰、水泥、外加剂和水，按标准ＪＧＪ５５设计配合比，其特征在于，以高钛重矿渣砂、渣石为混凝土粗细集料。

【技术特征摘要】

【专利技术属性】
技术研发人员：游天才，娄元涛，何奇，卢宏山，
申请(专利权)人：攀枝花环业冶金渣开发有限责任公司，
类型：发明
国别省市：51[中国|四川]