The invention relates to a high-strength waterproof gypsum block containing non-metal nanometer material and a preparation method thereof. It belongs to the field of building material technology. The utility model mainly solves the problems that the existing ordinary gypsum block has low water resistance, low strength and restricted use. It is mainly characterized by comprising the following steps: 1. in 35 to 40 parts by weight of water by adding 0.3 to 0.5 parts by weight of a hydrogen containing silicone oil; 2. add 0.005 to 0.01 parts by weight of eighteen alkyl three methyl ammonium chloride; 3. and then mixing 45 to 50 parts by weight of semi hydrated gypsum powder, 3 to 10 parts by weight of sepiolite powder and 3 to 5 parts by weight of munto powder added to the liquid; 4. into the mould box molding, mold, maintenance, to obtain high-strength waterproof gypsum block. Advantages: 1. waterproof effect reached 2 hours water absorption rate is below 5%, conversion coefficient is above 0.75; 2. improve the strength of 2-8 times, increase toughness. The invention is mainly used for frame type non load bearing wall, such as partition wall, partition wall, bathroom, kitchen, toilet, water tank and so on.
【技术实现步骤摘要】
本专利技术属于建筑材料
，具体涉及建筑物中砌筑非承重内墙用的石 膏砌块。
技术介绍
随着粘土砖的禁止使用，大量的替代产品相继打入建筑市场。石膏砌块作为一种环保绿色建材也快速地进入建筑行业；国家也相应发布了中华人民共和 国建材行业石膏砌块标准。目前市场上的普通石膏砌块，耐水性能低，它随着湿度的增加，石膏砌块 的强度急剧降低，材料蠕变性也逐渐增大，因此，在使用上受到限制。石膏耐 水性差的原因有三，其一是石膏有很大的溶解度；其二是石膏体的微裂纹吸湿; 其三是石膏材料的高孔隙加重吸湿。根据上述情况，国内外众多的单位和个人在石膏砌块防水的问题上开展了 大规模的研究和开发，如乳化沥青、石腊乳液、硅烷系列产品等的加入。上述 方法，要么价格高，要么降低了原来的强度，在实际生产中工艺复杂，得不到 良好的推广应用。
技术实现思路
本专利技术的目的就是针对上述不足之处而提供一种防水的、强度高的石膏砌 块及制备方法。本专利技术的目的是这样实现的本专利技术提供的含非金属纳米材料的高强度防水石膏砌块，其组成含有1、 45 50重量份的石膏粉；2、 3 10重量份的天然纳米级海泡石粉；3、...
【技术保护点】
一种含非金属纳米材料的高强防水石膏砌块，其特征在于：含有：４５～５０重量份半水石膏粉；３～１０重量份的天然纳米级海泡石粉；３～５重量份的天然纳米级蒙托石粉；０．３～０．５重量份的含氢硅油；０．００５～ ０．０１重量份十八烷基三甲基氯化铵。
【技术特征摘要】
【专利技术属性】
技术研发人员：李雨加，徐朝富，
申请(专利权)人：李雨加，徐朝富，
类型：发明
国别省市：85[中国|重庆]