The invention provides a method for preparing silicate cement clinker by using fluorite tailings, which relates to the preparation of Portland cement clinker. It is characterized in that the tailings containing CaF down 2 weight percent 435% by crushing and CaCO: 3 and Al: 2 O: 3 ~ 34%, 32 mixed according to 65 ~ 67%, 0.2 ~ 1% weight percent of the calcined temperature subsection to 12-13, mechanical grinding 0.074mm standard sieve that is, by the invention of cement clinker. Add the amount of tailings in the invention > 30%, is more effective way to reduce the volume and quantity of tailings, have to solve the problem of land occupation and environment pollution of tailings, tailings and existing components: CaF 2 can be used as mineralizer, lower sintering temperature.
【技术实现步骤摘要】
本专利技术涉及一种硅酸盐水泥熟料的制备方法，尤其涉及一种利用含萤石尾矿的水泥熟 料制备方法。
技术介绍
现我国各类矿山堆存的尾矿已达50多亿吨，并以年排放3亿多吨的速度在增长，其 中含萤石尾矿的量也十分惊人。仅武义县萤石尾矿数量已达300多万吨，需要占用20多 万平方米场地进行堆放，每天还要新增尾矿900吨左右。湖南柿竹园多金属矿号称"世界 有色金属博物馆"，含数十种有用元素，但目前仅回收Pb、 Zn、 W、 Mo、 Bi、 Cu，尾矿 中有大量有用矿物未回收利用，如萤石和石榴石。尾矿废弃会造成资源的浪费，而且含萤 石尾矿的堆放会给环境遗留安全隐患。含萤石尾矿随着雨水冲刷，导致水中氟化钙含量超 标，这样的污水流入农田，使土地板结，影响作物生长；污水渗入地下，会造成地下水污 染。因此含萤石尾矿的有效利用可以解决尾矿堆积沉淀造成的占地问题，同时有助于消除 环境灾害隐患。大多数矿山尾矿的主要矿物成分由硅酸盐、铝硅酸盐、碳酸盐矿物组成，化学成分以 Si02、 A1203、 CaO、 MgO、 Fe203、 K20、 Na20为主，是建筑、陶瓷、玻璃工业的重要矿 物原料...
【技术保护点】
一种利用含萤石尾矿制备硅酸盐水泥熟料的方法，其特征在于：制备工艺步骤为：ａ、将含萤石尾矿原料机械粉碎过０．０７４ｍｍ标准筛，将筛下尾矿粉末、ＣａＣＯ↓［３］、Ａｌ↓［２］Ｏ↓［３］按照３２～３４％、６５～６７％、０．２～１％的重量百分比混合；ｂ、混合料中加入重量百分比为２～６％的无水乙醇，在常温下使用行星磨研磨６～１０小时，将生料混合均匀；ｃ、将生料装入刚玉方舟置于高温炉中，以１０～２０℃／ｍｉｎ的升温速率升温至７００－１１００℃，保温０．５－１．５小时；再以５－１０℃／ｍｉｎ的升温速率升温至１２００－１３００℃，保温０．５～３小时，然后取出物料，在空气中冷却至室温；ｄ、冷...
【技术特征摘要】
【专利技术属性】
技术研发人员：连芳，郭玉娟，徐利华，
申请(专利权)人：北京科技大学，
类型：发明
国别省市：11[中国|北京]