The invention relates to a building material concrete admixture, in particular to a flour milling paste of a polycarboxylate superplasticizer. The present invention by weight of its basic components: polycarboxylate superplasticizer solution 30 ~ 40%, sodium lignosulfonate (SL) 15 ~ 25%, 10 ~ 20% calcium nitrite, maltodextrin 3 ~ 5%, sodium thiosulfate (soda) from 10 to 12%, distilled water 10 ~ 20%. The present invention is a liquid and high temperature resistant, economical and easy to paste powder, solved by polycarboxylate superplasticizer solution directly in the milling process, high viscosity, easy to appear easy difficulty sticking, high temperature, easy combustion is not easy to powder.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料""一混凝土外加剂，特别是一种聚羧酸 盐高效减水剂的制粉浆体。技术背景聚羧酸盐高效减水剂，由于其优异的性能指标和特点，是以萘系 为主体的第二代混凝土外加剂的升级换代产品。该类产品目前国内均 为液剂，其在工程使用中存在掺量大、包装和运输成本高、使用半径 小、现场施工掺用量不易计量等不足。然而聚羧酸盐高效减水剂粉剂， 目前国内处于空白。
技术实现思路
本专利技术所要解决的技术问题是将经化学合成的聚羧酸盐高效减 水剂液剂，复配制成一种可以制粉的浆体，解决用聚羧酸盐高效减水 剂液剂在直接制粉过程中，易出现的高黏度、易粘壁、不耐高温、易 燃烧等不易成粉的难点，配制一种既有流动性又耐高温，既经济又易制粉的浆体，将其制成的聚羧酸盐高效减水剂粉剂。聚羧酸盐高效减 水剂粉剂与水剂相比，技术性能更加优异和使用效果更为显著，经济 效益更为突出，这是本专利技术的关键所在。本专利技术采用聚羧酸盐高效减水剂液剂和其他材料复配制成的喷粉浆体，按重量计其基本组成为聚羧酸盐高效减水剂液剂(固含量20%) 30~40%木质素磺酸钠(木钠) 15~25%亚硝酸转 10 20%麦芽糊精 3 5%硫代硫酸钠(大苏打) 10~12%蒸馏水 10~20% 应用聚羧酸盐高效减水剂液剂和其他材料，复配制成的喷粉浆体配比实例如下配比1聚羧酸盐高效减水剂液剂(固含量20%) 30%木质素磺酸钠(木钠) 25%亚硝酸钙 10%麦芽糊精 5。/。硫代硫酸钠(大苏打) 10%蒸馏水 20% 配比2聚羧酸盐高效减水剂液剂(固含量20%) 35%20%亚硝酸钓 15%麦芽糊精 4%硫代硫酸钠...
【技术保护点】
一种可制成聚羧酸盐高效减水剂粉剂的浆体，其特征是：按重量计其基本组成为 聚羧酸盐高效减水剂液剂 ３０～４０％ 木质素磺酸钠（木钠） １５～２５％ 亚硝酸钙 １０～２０％ 麦芽糊精 ３～５％ 硫代硫酸钠（大苏打） １０～１２％ 蒸馏水 １０～２０％。
【技术特征摘要】
【专利技术属性】
技术研发人员：陈国忠，
申请(专利权)人：陈国忠，陈炜，彭振华，邱晓蓉，姜海东，
类型：发明
国别省市：32[中国|江苏]