A modified cement grinding agent, which consists of the following parts by weight of raw material: 1 maleic acid 1.5, calcium lignosulfonate 0.6 0.9 copies, 14 copies of silica 8, fly ash 6 sodium acetate 2 12 copies, 4 copies, 7 copies of 6 triethanolamine, hydroxyethylidene two phosphoric acid 2 4 copies, 3 copies of 5 wine stone acid, sodium carbonate, 12 22 copies, 13 copies of 7 ammonium chloride, potassium hydroxide and 10 glycol 7 20 copies, 11 copies, 3 polycarboxylate superplasticizer 7, bentonite 6 9 sodium thiocyanate, 8 15. The invention has the advantages that: the improved cement grinding aid of the invention can improve the performance and quality of cement, effectively improve the utilization rate of energy in the cement milling process, has good performance and can reduce the energy consumption.
【技术实现步骤摘要】
本专利技术涉及一种改良型水泥助磨剂。
技术介绍
水泥行业是资源消耗大户，不仅大量消耗石灰石等矿物资源，而且对煤炭等能源资源需求量巨大，水泥工业面临着严峻的资源问题。所以水泥助磨剂对于水泥加工非常重要，可以改善水泥流动性，提高磨机的研磨效果和选粉机的选粉效率，从而降低粉磨能耗，有效节约资源。但目前市场上的助磨剂还存在一些不足，成本较高，用量大，作用小，有待于进一步改善。
技术实现思路
针对现有技术的不足，本专利技术要解决的问题是，提供一种改良型水泥助磨剂，改善水泥的性能和品质，有效提高水泥磨粉过程中能量的利用率，性能优良，降低能源的消耗。为解决现有技术问题，本专利技术提供的技术方案是，一种改良型水泥助磨剂，其由以下重量份数的原料制成：马来酸1-1.5份，木质素磺酸钙0.6-0.9份，二氧化硅8-14份，粉煤灰6-12份，醋酸钠2-4份，三乙醇胺6-7份，羟基乙叉二磷酸2-4份，酒石酸3-5份，碳酸钠12-22份，氯化铵7-13份，氢氧化钾10-20份，二醇7-11份，聚羧酸盐减水剂3-7份，膨润土6-9份，硫氰酸钠8-15份。本专利技术的有益效果是：本专利技术的改良型水泥助磨剂，改善水泥的性能和品质，有效提高水泥磨粉过程中能量的利用率，性能优良，降低能源的消耗。具体实施方式实施例1一种改良型水泥助磨剂，其由以下重量份数的原料制成：马来酸1份，木质素磺酸钙0.6份，二氧化硅8份，粉煤灰6份，醋酸钠2份，三乙醇胺6份，羟基乙叉二磷酸2份，酒石酸3份，碳酸钠12份，氯化铵7份，氢氧化钾10份，二醇7份，聚羧酸盐减水剂3份，膨润土6份，硫氰酸钠8份。实施例2一种改良型...
【技术保护点】
一种改良型水泥助磨剂，其特征在于：其由以下重量份数的原料制成：马来酸1‑1.5份，木质素磺酸钙0.6‑0.9份，二氧化硅8‑14份，粉煤灰6‑12份，醋酸钠2‑4份，三乙醇胺6‑7份，羟基乙叉二磷酸2‑4份，酒石酸3‑5份，碳酸钠12‑22份，氯化铵7‑13份，氢氧化钾10‑20份，二醇7‑11份，聚羧酸盐减水剂3‑7份，膨润土6‑9份，硫氰酸钠8‑15份。
【技术特征摘要】
1.一种改良型水泥助磨剂，其特征在于：其由以下重量份数的原料制成：马来酸1-1.5份，木质素磺酸钙0.6-0.9份，二氧化硅8-14份，粉煤灰6-12份，醋酸钠2-4份，三乙醇胺6-...
【专利技术属性】
技术研发人员：徐茂航，
申请(专利权)人：青岛百千川海洋生态科技有限公司，
类型：发明
国别省市：山东;37
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。