The invention relates to a building material, in particular to a join in the concrete mixing process of concrete with admixture plastic collapse performance. The present invention is basically made up of sodium gluconate 30 - 40%, sodium tripolyphosphate 30 - 40%, soft white sugar 20 - 25%, citric acid 5 - 10%. The invention can reduce the concrete because of its component materials and the temperature, humidity, and the variation of the concrete performance index, the adaptability of cement is more extensive, can effectively reduce the concrete mixing process in a variety of plastic materials were added to security collapse trouble, the production cost is lowered obviously.
【技术实现步骤摘要】
本专利技术涉及一种建筑材料,特别是一种在混凝土拌和过程中加入 的对混凝土具有保塌保塑性能的外加剂。技术背景混凝土随组分材料的变化(特别是水泥)和气温、湿度的变化, 其性能指标会产生较大的变异,为了减小这种变异,工程中采取掺加 混凝土保塌保塑剂的措施,使混凝土符合设计技术要求和施工操作要 求。目前,国内工程中常采取掺加单一的葡萄糖酸钠、三聚磷酸钠、 绵白糖、柠檬酸等保塌保塑材料,也有各种各样搭配使用葡萄糖酸钠、 三聚磷酸钠、绵白糖、柠檬酸等保塌保塑材料的方法,但是保塌保塑 的技术指标不理想,成本偏高。本专利技术采用葡萄糖酸钠、三聚磷酸钠、 绵白糖、柠槺酸等保塌保塑材料进行复配,集各组分的单一功能为复 合多功能,使其产生复合效应,因而对水泥的适应性更加广泛,更能 有效地减少混凝土拌和过程中多品种保塌保塑材料分别加入的麻烦, 从而避免差错的发生,同时生产成本也明显降低。
技术实现思路
本专利技术所要解决的技术问题是提供一种复配混凝土保塌保塑剂, 掺加该混凝土保塌保塑剂,可以减小混凝土因其组分材料和气温、湿 度变化,而产生混凝土性能指标的变异,达到理想的效果。本专利技术的混凝土保塌保塑剂,按重量计其基本组成为葡萄糖酸钠 30 40%三聚磷酸钠 30 40%绵白糖 20~25% 柠檬酸 5 10% 本专利技术混凝土保塌保塑剂其复配实例如下 配比1葡萄糖酸钠 30%三聚磷酸钠 40%绵白糖 20°/。柠檬酸 10% 配比2葡萄糖酸钠 35%三聚磷酸钠 35%绵白糖 25% 柠檬酸 5% 配比3葡萄糖酸钠 40%三聚磷酸钠 30%绵白糖 25%柠檬酸 5%本专利技术的 ...
【技术保护点】
一种在混凝土拌和过程中加入的对混凝土具有保塌保塑性能的外加剂,其特征是:按重量计其基本组成为: 葡萄酸钠 30~40% 三聚磷酸钠 30~40% 绵白糖 20~30% 柠檬酸 20~30%。
【技术特征摘要】
【专利技术属性】
技术研发人员:陈国忠,
申请(专利权)人:陈国忠,陈炜,彭振华,邱晓蓉,姜海东,
类型:发明
国别省市:32[中国|江苏]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。