The invention discloses a blank for manufacturing bakeware ceramic products, the glaze and its products, blank containing kaolin, talc, feldspar and limestone, in addition to containing blank accounted for the total weight of 10 to 28% of the waste glass, glaze mainly by low temperature frit, feldspar, quartz and calcite, the blank is made of ceramic body, coated on the surface of the glaze, by 1060 to 1150 DEG C firing, the invention can obtain tray ceramic products. The present invention makes full use of glass waste material and has low firing temperature. The ceramic product made by the utility model can be quenched without quenching after 280 DEG dry burning, and the glaze surface does not appear fog after the use of dry burning and rapid cooling.
【技术实现步骤摘要】
本专利技术涉及陶瓷原材料及其陶瓷制品，具体是用于制造烤盘类陶瓷产 品的坯料、相应的釉及其制成的烤盘类陶瓷产品。
技术介绍
在节能环保要求日益提高的新形势下，对日用陶瓷产业提出了更高的 要求，日用陶瓷行业要朝着可持续发展的方向前进，企业就必须做到节能 减排，产品经济环保，提高市场竞争力。为了发展，企业应该加大科研力 度，进行技术创新，争取在生产方面有更大的突破。适合微波炉、烤箱使用，同时可以进行机械化洗漆的烤盘类陶瓷产品， 要求具有良好的抗淬裂、抗急冷性能和机械强度。传统的烤盘类陶瓷产品 热稳定性能差，急热急冷时易淬裂，不能干烧。目前此类产品热交换值20 18(TC左右，干烧超过18(TC后急冷就会开裂，由于此类产品烧成温度基 本在1160 123(TC之问，烧成温度较高导致其色彩单调，装饰性、观赏性较 差。中国专利公开说明书CN1230528A公开一种陶瓷材料组合物，是在陶 瓷配方中加入立体四针状氧化锌晶须来提高陶瓷材料的抗淬裂和抗急冷性 能，但为了使立体四针状氧化锌晶须不被破坏，混合、研磨工艺要求高， 难以控制，对废品的利用也没有作出贡献。CN1155525...
【技术保护点】
用于制造烤盘类陶瓷产品的坯料，含有高岭土、滑石、长石和石灰石，其特征在于，还含有占坯料总重量１０～２８％的废玻璃，该坯料按重量百分比主要含有：ＳｉＯ↓［２］５４～７６％，Ａｌ↓［２］Ｏ↓［３］１４～２３％，ＣａＯ１～３％，ＭｇＯ１～３％，Ｋ↓［２］Ｏ和／或Ｎａ↓［２］Ｏ１～４％，Ｂ↓［２］Ｏ↓［３］２～４％，Ｌｉ↓［２］Ｏ０～１％，ＢａＯ０～１％，ＺｎＯ０～１％，ＳｒＯ０～１％，ＴｉＯ↓［２］０～１％，以及３～７％的烧失量。
【技术特征摘要】
【专利技术属性】
技术研发人员：章岳雄，吴宏彬，陈金铁，陈金生，林长，章永坚，
申请(专利权)人：潮州市雄佳陶瓷制作有限公司，
类型：发明
国别省市：44[中国|广东]