一种纳米级远红外陶瓷粉及其制备方法技术

本发明专利技术涉及一种纳米级远红外陶瓷粉及其制备方法，它主要是由纳米氧化锌、纳米氧化钛、纳米氧化钇、纳米氧化锆、纳米氧化铝、纳米氧化铜、纳米氧化镍、纳米氧化钴、纳米氧化硅、超细电气石粉、和超细碳化硅粉等组分合成，纳米复合金属氧化物的粒径为２０～６０ｎｍ，电气石及碳化硅的粒径不大于０．５ｕｍ，其制备工艺采用液相沉淀法，工艺流程为：配料→溶解→加表面活性剂→沉淀→过滤水洗→脱水处理→干燥→气流粉碎→高温合成→过筛→性能检测→备用，目的是克服目前国内单晶红外粉体及复合红外粉体发射强度较低的缺陷。

Nanometer far infrared ceramic powder and preparation method thereof

The invention relates to a nanometer far-infrared ceramic powder and preparation method thereof, which is mainly composed of nano Zinc Oxide, nanometer titania, yttrium oxide, zirconium oxide, nano alumina, nano copper oxide, nano nickel oxide, cobalt oxide, nano nano silicon oxide, superfine powder, electrical and ultrafine silicon carbide powder. Synthesis, nano composite metal oxide particle size is 20 ~ 60NM, tourmaline and silicon carbide particle size less than 0.5um, its preparation process with liquid phase precipitation method, process for material mixing, dissolving, adding surfactant, precipitation, filtering and washing, dehydration treatment, drying, crushing, synthetic, high temperature air screening, performance testing, spare, purpose is currently the single crystal infrared powder and composite infrared powder with low strength to overcome the defect emission.

【技术实现步骤摘要】

本专利技术涉及一种纳米级远红外陶瓷粉，特别涉及一种高效红外陶瓷粉体的制备方法，属 于功能材料制造领域。
技术介绍
远红外陶瓷粉是由无机矿物、非金属氧化物和金属氧化物制造而成，红外辐射技术发展 的实质就是研究得到足够强度的红外辐射，其核心是研制高辐射率的材料，材料的红外辐射 是因其粒子振动引起偶极矩变化而产生的。根据振动对称性选择定则粒子振动时的对称性 越低，偶极矩的变化就越大，其红外辐射就越强。由于陶瓷材料是由多原子组成的大分子结 构的物质，多原子在振动过程中易改变分子的对称性而使偶极矩发生变化，因此，许多陶瓷 材料都具有较高的辐射率，由此，近年来红外辐射陶瓷材料越来越受到人们的广泛重视，从 国内外研究情况来看，前苏联、美国、日本及西欧一些学者在二十世纪60、 70年代就对一些 具有优良辐射特性的化合物单晶如Si02 SiC、 Fe203、 Ti02等氧化物的透射光谱、反射光谱 及辐射特性进行了较为细致的理论研究，但实用型的红外辐射陶瓷材料的开发与应用则直到 二十世纪70、 80年代才真正开始。二十世纪80年代以来，材料学家们提出了一种全新的红 外辐射陶瓷的设计思想一材料复合的思本文档来自技高网...

【技术保护点】
一种纳米级远红外陶瓷粉及其制备方法，其特征在于：它是由以下配比的组分组成：　纳米氧化锌２８～５０％，纳米氧化钛３～６％，纳米氧化钇２～１０％，纳米氧化锆５～９％，纳米氧化铝２～６％，纳米氧化铜２～６％，纳米氧化镍２～５％，纳米氧化钴２～４％，纳米氧化硅３～６％，超细电气石粉６～１５％，超细碳化硅粉２～５％。

【技术特征摘要】

【专利技术属性】
技术研发人员：胡国庆，
申请(专利权)人：胡国庆，
类型：发明
国别省市：81[中国|广州]