The invention relates to a magnesium calcium RH dipping tube heat spraying feeding material for high performance smelting silicon steel and a preparation method thereof. It is characterized by high purity magnesia and synthetic Doloma is mainly composed of composite wood; sulfonic acid calcium, modified starch ether soft clay and water glass as a low melting organic additive to replace conventional gunning material by the use of harmful plasticizers, to achieve good spray gunning material fill the adhesion and good high-temperature performance. And through the use of composite ultrafine MgO powder, SiO powder and calcium hydroxide: 2 powder two superfine powder to water reducing and reinforcing effect, further improve the adhesion and sintering of materials, improved materials and high temperature strength. The gunning material has high hot strength, high residue erosion and molten steel erosion of good performance, the RH device of special silicon steel smelting low sulfur impregnated tube after gunning service life of more than one furnace, to meet the special requirements of steel smelting.
【技术实现步骤摘要】
本专利技术涉及一种高性能冶炼硅钢用镁钙质RH浸渍管热喷补料及其配制 方法，具体地说本专利技术是为了提高硅钢冶炼精炼系统中RH浸渍管寿命，而 提供的一种镁钙质热喷补料。属于耐火材料领域。
技术介绍
随着冶炼新技术的出现，纯净钢的生产得到了迅速的发展。RH循环脱气法是炉外精炼方法的一种。它的主要原理是将真空脱气缸的上升管和下降管同时插入钢包钢液里，并在上升管的下端吹入氩气，使上升管和下降管相 互产生压降，钢液可通过上升管返入真空缸脱气，再通过下降管进入钢包， 在钢包中，下降管附近的钢液，不断地流向上升管，流动的钢液也不断洗刷 渣层底部，从而到达较好的脱硫效果，同时钢液在循环过程中也实现了脱气的目的。归纳起来RH精炼方法具有以下特点可以给钢水脱硫、脱气、脱氧、脱碳，还可以进行钢水成分调节，加热钢水等作用。正是RH精炼方法的多功能性，使得所用的耐火材料面临着极其苛刻的使用条件，如真空条 件下工作温度很高；间歇式操作温度波动很大；钢水循环流动的冲刷；高碱 度钢渣的侵蚀等等。在整个RH装置中浸渍管是RH装置使用寿命的关键， 为了达到使用要求国内外一般选用抗渣性优良、高温强...
【技术保护点】
一种冶炼硅钢镁钙质ＲＨ浸渍管热喷补料，其特征在于所述的热喷补料的质量百分组成为： 合成镁钙砂 ３～０ｍｍ ３０～６０％； 高纯镁砂 １～０ｍｍ ２０～６０％； 高纯细镁砂 ≤７５μｍ １０～３０％； 复合的超细粉粉体 ２～１０％； 外加聚磷酸盐有机结合剂 ０．１～３％； 有机添加剂 ０．１～３％； 有机防爆纤维 ０．０５～３％； 所述的复合超细粉料为高纯硅微粉、氢氧化钙微粉和氧化镁微粉中的二种或三种组成； 所述的有机添加剂为木质磺酸钙、木质磺酸镁、羟甲基纤维素钠和改性淀粉醚中的一种或几种复合组成。
【技术特征摘要】
【专利技术属性】
技术研发人员：李华坚，
申请(专利权)人：上海彭浦特种耐火材料厂，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。