The invention provides a roasting furnace chamber is made of refractory brick, dry part and additives, the dry part is: 10 ~ 5mm particle size of waste refractory brick materials from 32 to 37 parts by weight, size 5 ~ 3mm diameter waste refractory brick material is 22 to 26 parts by weight of 3mm, the particle size of waste refractory bricks the material is 8 ~ 12 weight and 180 to waste brick fines from 28 to 33 parts by weight of the additive for water glass solution, six sodium phosphate, sodium fluoride and steel fiber; the invention adopts waste clay brick as the main raw material for the preparation of refractory brick is roasting furnace chamber. The vibration molding directly molded in the preparation of the refractory brick itself, as a whole, even if the collision is not easy to generate dislocation, basically do not need to be repaired, using waste as raw material The utility model realizes the reuse of the resources and the waste to the valuables, meanwhile, the environmental pollution is reduced, the labor intensity of the workers is reduced, and the work efficiency is improved.
【技术实现步骤摘要】
本专利技术涉及一种焙烧炉室上口耐火大砖，同时涉及该耐火大砖的制备方法。
技术介绍
焙烧炉广泛应用于有色行业中，例如炭素企业等。在生产过程中，焙烧炉室上口的温度为250 10(XTC，企业所使用的焙烧炉室上口大都由异型黏土质耐火砖砌筑而成。但是在实践过程中发现使用耐火砖砌筑的焙烧炉室上口存在以下诸多缺陷l、需要使用多种型号的耐火砖来砌筑，砌筑耐火砖用的耐火泥与 耐火砖之间不能达到共同烧结，因此，砖与砖之间不能形成-个牢固稳定的整 体，在生产过程中，稍有不慎天车运送的炭块会与焙烧炉室卜.口发生碰撞，造 成焙烧炉室上口的耐火砖发生错位，耐火砖松动，导致火道的密闭性大大下降； 2、当焙烧炉室上口的耐火砖发生错位而松动，火道的密闭性差时，如果不及时 修理，势必会影响下一循环火道温度的调整，从而影响炭块的焙烧质量和合格 率，因此造成焙烧炉室上口维修频繁，维修费用增高，导致成本上升，工人的劳 动强度增大。当焙烧炉室上口因碰撞造成耐火砖损坏时则不能继续使用，只好将废耐火 砖丢弃，这样会造成环境污染，给环境保护带来巨大的压力，而且占用大量土 地。如何合理地利用这些工业废弃物也成...
【技术保护点】
一种焙烧炉室上口耐火大砖，其特征在于：由干料部分和添加剂制成，所述干料部分为：１０～５ｍｍ粒径的废耐火砖料３２～３７重量份、５～３ｍｍ粒径的废耐火砖料２２～２６重量份、３ｍｍ以下粒径的废耐火砖料８～１２重量份和１８０目的废耐火砖细料２８～３３重量份，所述添加剂为水玻璃溶液、六偏磷酸钠、氟硅酸钠和钢纤维，水玻璃溶液的加入量为干料部分总重量的１３～１５％、六偏磷酸钠的加入量为水玻璃溶液重量的０．３～０．６％、氟硅酸钠的加入量为水玻璃溶液重量的３．２～６．４％，钢纤维的加入量为干料部分总重量的０．５～１％。
【技术特征摘要】
【专利技术属性】
技术研发人员：刘兆勤，上官江水，范银贵，高明，葛社敦，
申请(专利权)人：河南中迈炭素有限公司，
类型：发明
国别省市：41[中国|河南]