The invention relates to a nanometer lanthanum doped barium ferrite film and its preparation method, characterized in that: the feature is the formula as follows: ethylene glycol 1.48 ~ 1.60g / 100mL, citric acid 2.51 ~ 2.71g / 100mL, 1.74g / 100mL, ferric nitrate, barium nitrate and lanthanum nitrate 0.125g / 100ml 0.03 ~ 0.125g / 100ml. The preparation method is using ferric nitrate, barium nitrate, lanthanum nitrate as raw materials by the sol-gel method to prepare precursor preparation of lanthanum doped nano barium ferrite; to clean silica as a substrate, ferric nitrate, barium nitrate, lanthanum nitrate, citric acid as complexing agent, ethylene glycol as auxiliary complexing agent that is for film formation by dipping coating method. The advantages of this method are: simple process, low cost; convenient preparation of thin films on various substrates with different shapes, by lanthanum doped barium ferrite nano film of high purity, can be used for the preparation of thin film magnetic recording materials, wave absorbing materials.
【技术实现步骤摘要】
本专利技术涉及一种，主要以硝酸铁、硝酸钡、 硝酸镧等为原料利用溶胶一凝胶法来制备镧掺杂纳米钡铁氧体的前驱体；以洁净的二 氧化硅为基片，硝酸铁、硝酸钡、硝酸镧为主盐，柠檬酸为络合剂，乙二醇为助络合 剂，采用浸渍-提拉法进行制膜。
技术介绍
目前对纳米钡铁氧体材料的研究表明，该材料存在吸波性能不理想、吸波频段有 待进一步拓宽的问题。稀土元素具有丰富的/层电子，其化合物本身就是具有优良 磁性能的吸波材料，因而稀土元素的掺入，必然会对钡铁氧体的整个体系吸波性能的 改善发挥较大的作用。目前，已有文献报道利用稀土元素的掺入来制备纳米钡铁氧体 粉体，但对纳米钡铁氧体吸波性能的改善作用并不理想。由于纳米钡铁氧体薄膜在垂 直磁记录、微波器件以及磁光存储方面诱人的应用前景，因而目前已有文献报道利用溅 射沉积、化学气相沉积来制备纳米钡铁氧体薄膜。纳米薄膜有多种制备方法，主要可分为物理方法和化学方法两大类。其中经常使 用的物理方法包括粒子束溅射沉积、磁控溅射沉积，以及新近出现的低能团簇束沉积法；化学方法包括(有机金属化合物)化学气相沉积(MOCVD)法、电沉积法、热解法 和溶胶-凝胶法...
【技术保护点】
一种镧掺杂纳米钡铁氧体薄膜，其特征在于配方如下：乙二醇１．４８～１．６０ｇ／１００ｍｌ、柠檬酸２．５１～２．７１ｇ／１００ｍｌ、硝酸铁１．７４ｇ／１００ｍｌ、硝酸钡０．１２５ｇ／１００ｍｌ和硝酸镧０．０３～０．１２５ｇ／１００ｍｌ。
【技术特征摘要】
【专利技术属性】
技术研发人员：黄英，杨永峰，齐暑华，李玉青，黄飞，
申请(专利权)人：西北工业大学，
类型：发明
国别省市：87[中国|西安]