The invention discloses a dry composite fireproof glass production using glass veneer laminating method, it includes the main process steps are as follows: two pieces of fireproof glass veneer layer is buckled; the load is connected with a vacuum pump in the vacuum rubber bag to maintain the pressure in the plastic bags of 100 to 950Pa lasts 30 to 60 minutes; the 50 - 100 DEG C hot air in the heating chamber 30 heating plastic bags for 60 minutes, while continuing to maintain pressure in the bag; to stop heating, heating indoor temperature to maintain the pressure inside the bag is reduced to 40 DEG C, close the vacuum pumping system; 5 to room temperature, trimming and finishing. The method is suitable for the production of laminated fireproof glass and has convenient operation and good quality inside and outside the product.
【技术实现步骤摘要】
本专利技术涉及在两片玻璃之间夹置无机材料而制成复合防火玻璃的合片方法。防火玻璃是一种玻璃深加工产品,具有防火、透光、透视等特点,广泛应用于高层建筑、展品陈列、防火隔断等方面。防火玻璃生产的一般工艺流程是玻璃切割、浇注防火液、干燥得到防火玻璃单板,再合片、修边,而形成防火玻璃。其中的合片是一道关键工序,直接决定着产品的最终质量。现行的防火玻璃合片方法采用湿法合片,即在两块防火玻璃单板合片时,通过使用复合液使两玻璃单板粘接在一起,形成防火玻璃。而湿法合片有以下弊端1、使胶合层中留有非常密集的微泡,影响视觉。2、所使用的复合液受挤压后从两单板中间流出,污染防火玻璃外表面,形成难以擦净的白霜,影响成品的外观质量。3、胶合层中水份含量过高,在以后的使用中易脱胶、起泡,缩短了产品的使用寿命。4、因为复合液是滑腻的碱性油状物,湿法合片中玻璃的搬运等操作受到一定的影响,易出现滑脱现象。本专利技术的目的在于针对上述现有湿法合片技术存在的问题,而提供一种,从而避免湿法合片防火玻璃带来的缺陷。为实现上述目的,本专利技术提供了一种,它使用单面附置无机防火胶层的防火玻璃单板,该方法包括下述次序的工艺步骤①将两块防火玻璃单板的胶层面相扣合,周边对齐;②装入一接有真空泵的橡胶袋中抽真空维持胶袋内气压100-950Pa,持续30-60分钟;然后,③用50-100℃热空气干加热室内加热胶袋30-60分钟,同时继续保持袋内压力;④停止加热,维持袋内压力至加热室内温度降至40℃,关闭真空抽气系统;⑤降至室温,修边整理。本合片方法抽真空时维持胶袋内气压的首选值为100Pa,持续时间为30分 ...
【技术保护点】
一种复合防火玻璃的干法合片方法,使用单面附置无机防火胶层的防火玻璃单板,其特征是:该方法包括下述次序的工艺步骤:①将两块防火玻璃单板的胶层面相扣合,周边对齐;②装入一接有真空泵的橡胶袋中抽真空:维持胶袋内气压100-950Pa,持续 30-60分钟;然后,③用50-100℃热空气于加热室内加热胶袋30-60分钟,同时继续保持袋内压力;④停止加热,维持袋内压力至加热室内温度降至40℃,关闭真空抽气系统;⑤降至室温,修边整理。
【技术特征摘要】
【专利技术属性】
技术研发人员:耿平,马军,
申请(专利权)人:中国耀华玻璃集团公司,
类型:发明
国别省市:13[中国|河北]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。