The invention discloses a method for on-line production of float glass coating, using chemical vapor deposition technology on the glass surface at different temperatures will diborane and silane, ethylene and carbon dioxide, with inert gas as the carrier. The plasmid mixed flow, have been deposited with two layers of shielding layers, the two layer shielding layer with gradient refractive index gradient. To reduce reflection in subsequent coating glass coating prepared by the invention of the functional layer and color saturation, can be eliminated by reflectance and color saturation caused by the rainbow, at the same time, the glass block migration of alkali metal ions to the functional layer, prevent functional film contamination.
【技术实现步骤摘要】
本专利技术涉及，尤其涉及利用化学汽相沉积技术，浮法在线生产折射率梯度变化并具有屏蔽作用的涂层玻璃的方法。
技术介绍
现有的在浮法玻璃生产线上生产镀膜玻璃的方法有很多种，镀膜玻璃不但要具有各种功能，如低辐射功能、自清洁功能，而且还要具有良好的视觉效果，较高的反射比和比较浓厚的外观色彩都是建筑上不能接受的。为了达到赏心悦目的视觉效应，并阻止玻璃中碱金属离子从玻璃表层向外迁移，在玻璃表面和功能层之间沉积一层或多层中间层(屏蔽层)，以降低功能层的反射比和色彩饱和度。从光学膜系匹配的原理出发，玻璃表面和功能层之间的折射率应该是渐变的。目前常用的方法是在玻璃和功能层之间，沉积一层屏蔽层，如中国专利CN 87101283公开的是通过硅烷、不饱和烃和二氧化碳的气体混合物在热玻璃表面上只沉积一层底层(屏蔽层)。这种玻璃折射率变化的梯度较大，最终的产品反射色的色饱和度较高，不能有效消除彩虹的缺点。
技术实现思路
本专利技术的目的是为生产无色透明、具有折射率梯度变化的屏蔽层的镀膜玻璃而提供一种。本专利技术的，包括以下步骤1)在浮法玻璃生产线锡槽中，将乙硼烷、硅烷、乙烯、二氧化碳，以惰性...
【技术保护点】
浮法在线生产涂层玻璃的方法，包括以下步骤：１）在浮法玻璃生产线锡槽中，将乙硼烷、硅烷、乙烯、二氧化碳，以惰性气体为载体组成前质体混合气流，利用化学汽相沉积法在温度为６７０～６９０℃的热玻璃表面沉积一层屏蔽层，乙硼烷∶硅烷∶乙烯∶二氧 化碳的体积比为０．００１～０．００１∶１∶３．５～４．５∶３．５～４．５；２）在浮法玻璃生产线锡槽中，将乙硼烷、硅烷、乙烯、二氧化碳，以惰性气体为载体组成前质体混合气流，利用化学汽相沉积法在温度为６４５～６６５℃的热玻璃的屏蔽层表面 再沉积第二层屏蔽层，乙硼烷∶硅烷∶乙烯∶二氧化碳的体积比为０．０００１～０．００１∶...
【技术特征摘要】
【专利技术属性】
技术研发人员：汪建勋，刘军波，韩高荣，刘起英，王伟，赵年伟，赵明，应益明，
申请(专利权)人：浙江大学蓝星新材料技术有限公司，
类型：发明
国别省市：86[中国|杭州]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。