用于基板的高应变点玻璃组合物制造技术

本发明专利技术涉及一种玻璃基板组合物，其含有ＳｉＯ↓［２］５５～７０ｗｔ％、Ａｌ↓［２］Ｏ↓［３］０～１ｗｔ％、ＺｒＯ↓［２］０．１～５ｗｔ％、Ｎａ↓［２］Ｏ０．１～５ｗｔ％、Ｋ↓［２］Ｏ７～１３ｗｔ％、ＭｇＯ７～１４ｗｔ％、ＣａＯ０～４ｗｔ％、ＳｒＯ７～１２ｗｔ％和ＳＯ↓［３］０．０１～０．５ｗｔ％。通过使用上述组合物制备的玻璃基板由于其应变点为至少５７０℃，在高温下的焙烧过程中显示出低的热变形，由于低于１４６０℃的熔点，没有例如燃料成本增加和耐火材料寿命周期短这样的缺点，并在５０～３５０℃的温度范围具有８０～９５×１０↑［－７］／℃的热膨胀系数。因此，根据本发明专利技术的玻璃适于用作基板。

High strain point glass composition for substrates

The invention relates to a composition comprising a glass substrate, SiO: 2, Al: 55 ~ 70wt% 2 O: 3, ZrO: 0 ~ 1wt% 2 ~ 5wt% 0.1, Na 2 ~ O0.1: 5wt%, K: 2 O7 ~ 13wt%, MgO7 ~ 14wt% CaO0, 4wt%, SrO7 ~ 12wt% ~ 3 and SO: 0.01 ~ 0.5wt%. Through the glass substrate using the composition due to the strain point of at least 570 DEG C, showing low thermal deformation at high temperature in the roasting process, because of lower than 1460 DEG C melting point, no such as fuel costs and short cycle life of refractory such shortcomings, and at 50 to 350 DEG C temperature range is 80 ~ 95 * 10 = 7 / C: the coefficient of thermal expansion. Accordingly, the glass according to the present invention is suitable for use as a substrate.

【技术实现步骤摘要】
【国外来华专利技术】

【技术保护点】
一种玻璃组合物，其含有ＳｉＯ↓［２］５５～７０ｗｔ％、Ａｌ↓［２］Ｏ↓［３］０～１ｗｔ％、ＺｒＯ↓［２］０．１～５ｗｔ％、Ｎａ↓［２］Ｏ０．１～５ｗｔ％、Ｋ↓［２］Ｏ７～１３ｗｔ％、ＭｇＯ７～１４ｗｔ％、ＣａＯ０～４ｗｔ％、ＳｒＯ７～１２ｗｔ％和ＳＯ↓［３］０．０１～０．５ｗｔ％。

【技术特征摘要】
【国外来华专利技术】...

【专利技术属性】
技术研发人员：李振赫，李时懋，李宰旭，
申请(专利权)人：株式会社KCC，
类型：发明
国别省市：KR[韩国]