The invention relates to a method for manufacturing an optical fiber preform. SiCl: 4, BBr: 3, freon, oxygen, hydrogen and helium as the raw material, the quartz tube deposition fluorine boron Co doped cladding layer and the reflecting layer, and then deposited in the core layer. When the core layer is doped with hydrogen, the different hydroxyl content is formed in the core layer by adjusting the ratio of hydrogen to the mixture gas in the tube. The invention can be prepared for different wavelengths (200 ~ 400nm) of the high transmittance of UV optical fiber, the wavelength of 308nm transmittance was 90 ~ 95%, in 254nm, up to 6575%.
【技术实现步骤摘要】
本专利技术涉及一种光纤预制棒的制造方法。紫外传输光纤要求羟基的含量达1400～1500PPm，而目前制造光纤的几种方法对于羟基的含量均难以控制调节，或达不到上述含量，使得紫外传输光纤的性能不理想。本专利技术的目的在于提供一种制造紫外光纤预制棒的方法，使得其羟基含量可以控制和调节。附附图说明图1为本专利技术汽相沉积装置示意图。附图2为本专利技术所述紫外光纤预制棒横断面结构示意图。附图3为本专利技术所述预制棒羟基含量与透过率的关系(254nm)附图4为两种不同羟基含量的光纤在紫外区透过率的比较，曲线A含有1200PPm羟基，曲线B含有200PPm羟基。如附图1所示，本专利技术所用汽相沉积装置由氢气入口1、氦气入口2、氟氯烷入3、O2入口4、SiCl4入口5、BBr3入口6、气体流量控制器7、旋转连接器8、玻璃车床9、氢氧焰燃烧器10等部分构成，其中石英管11夹在玻璃车床9上并与旋转连接器8相接，旋转连接器8在石英管11于玻璃车床9上旋转时，可使气体流量控制器7不旋转，氢氧焰燃烧器10可在玻璃车床9上沿石英管11的长度方向左右移动。如附图2所示，本专利技术所述预制...
【技术保护点】
一种紫外激光传能光纤预制棒的制造方法，其特征在于：所述的预制棒通过对石英管的不断旋转、注入混合气体、移动加热等步骤在石英管的内壁先沉积反应光层再沉积芯层，最后经过高温熔烧缩制而成，其中所述沉积反光层时的混合气体为ＳｉＣｌ↓［４］１００～１０００ｍｌ／ｍｉｎ、ＢＢｒ↓［３］１５０～１５００ｍｌ／ｍｉｎ、Ｏ↓［２］３００～２０００ｍｌ／ｍｉｎ、氟氯烷２～２００ｍｌ／ｍｉｎ，沉积芯层时的混合气体为ＳｉＣｌ↓［４］１００～１０００ｍｌ／ｍｉｎ、Ｏ↓［２］５００～２０００ｍｌ／ｍｉｎ、Ｈ↓［２］５～３００ｍｌ／ｍｉｎ、Ｈｅ１００～５００ｍｌ／ｍｉｎ，其中氢气与混合气体为体积比为０．１...
【技术特征摘要】
【专利技术属性】
技术研发人员：孙明武，高祀建，顾真安，
申请(专利权)人：中国建筑材料科学研究院，
类型：发明
国别省市：11[中国|北京]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。