The invention relates to an adhesive, which comprises the following components and quality copies: acrylate adhesive 100, crosslinking agent 1 ~ 2, 3 ~ 8 copies of the above additives; acrylate adhesive to FPC plate adhesion is 12 ~ 20gf/25mm, the auxiliary nonionic surfactant; also relates to the use of FPC the protective film and preparation method of the adhesive. The present invention by adding additives in adhesives, making use of the adhesive for FPC protective film adhesive layer to obtain ultra low viscosity and high temperature and pressure have the characteristics of bubble, the maneuverability is stronger so that the protective film and FPC joint, higher yield, lower production costs, improve production efficiency.
【技术实现步骤摘要】
本专利技术涉及保护膜领域,具体涉及一种低粘性、高温压合无气泡的胶黏剂,以及应用该胶黏剂FPC保护膜及制备方法。
技术介绍
柔性印刷线路板(FPC)具有可挠曲和缩小体积的特性,可满足电子产品短、小、薄、轻的要求,因此广泛应用于电子产品领域,如通讯设备、数码相机和摄影机、汽车电子、液晶图像显示等,通常FPC上需要覆盖一层保护膜来实现铜面的保护。现有的FPC保护膜种类繁多,但普遍都存在着以下问题:首先,FPC保护膜与FPC板贴合时,由于胶面有粘性,所以对于粘性较大的保护膜,手工贴合很容易造成贴合不平整、出现气泡等问题的发生,导致产品的报废,特别是对于那些很薄的保护膜,可操作性极差;然而,即使上述问题均能通过自动贴合机器得到解决,但在随后的高温压合中也会发生因保护膜与FPC板局部分开所致的气泡问题,这样不仅会增加生产成本,相应地,也会降低生产效率。
技术实现思路
本专利技术所要解决的第一技术问题是针对现有技术而提供一种低粘性且高温压合无气泡的胶黏剂组合物。本专利技术所要解决的第二个技术问题是针对现有技术而提供一种应用上述胶黏剂组合物的、低粘性且高温压合无气泡的FPC保护膜。本专利技术所要解决的第三个技术问题是针对现有技术而提供上述FPC保护膜的制备方法。本专利技术解决第一个技术问题所采用的技术方案为:一种胶黏剂组合物,其特征在于,其由以下组分及其质量份数组成:丙烯酸酯胶黏剂100份交联 ...
【技术保护点】
一种胶黏剂,其特征在于,其由以下组分及其质量份数组成:丙烯酸酯胶黏剂 100份交联剂 1~2份助剂 3~8份;上述丙烯酸酯胶黏剂对FPC板的粘着力为12~20gf/25mm,上述助剂为非离子型表面活性剂。
【技术特征摘要】
1.一种胶黏剂,其特征在于,其由以下组分及其质量份数组成:
丙烯酸酯胶黏剂100份
交联剂1~2份
助剂3~8份;
上述丙烯酸酯胶黏剂对FPC板的粘着力为12~20gf/25mm,上述助剂为非离子型表
面活性剂。
2.如权利要求1所述的胶黏剂,其特征在于,所述非离子型表面活性剂为烷基酚
聚氧乙烯醚、聚氧乙烯脂肪醇醚、聚氧乙烯聚氧丙烯嵌段共聚物、十六酸异丙酯、失水
山梨醇脂肪酸酯及蔗糖酯中的一种或多种。
3.如权利要求1所述的胶黏剂,其特征在于,所述交联剂为异氰酸酯类交联剂,
并为甲苯二异氰酸酯、二甲苯二异氰酸酯、二苯基甲烷二异氰酸酯、六亚甲基二异氰酸
酯、二环己基甲烷二异氰酸酯、三甲基环己基二异氰酸酯中的一种或多种。
4.一种应用有上述任一权利要求所述胶黏剂的...
【专利技术属性】
技术研发人员:周靖,陆建贤,王旭辉,
申请(专利权)人:宁波大榭开发区综研化学有限公司,
类型:发明
国别省市:浙江;33