The invention discloses a method for manufacturing a non aging hardness standard samples, the method for the steel coil cutting head and tail cut processing were removed two winding circle, the coil cutting edge processing for the steel coil contact with one side of the conveying belt, the other side was 150mm 250mm resection. This method overcomes the traditional hardness standard due to defects caused by the short period of aging, long-term stability of long-term effective monitoring of hardness, and batch production of samples with the same nominal value, facilitate the implementation of multiple hardness statistic analysis of monitoring value.
【技术实现步骤摘要】
本专利技术涉及一种无时效硬度标样的制作方法。
技术介绍
要保证布氏硬度、维氏硬度和洛氏硬度的测量精度,需要确保硬度计的测量精度;而要保证硬度计的测量精度,通常主要采用两方面的措施,第一通过直接校验和间接校验保证硬度计的溯源性;第二在每天进行硬度测量前,使用硬度标样监测设备的稳定性。目前市场上购买的硬度标样监测硬度计的长期稳定性存在以下两个问题:一、因为通常采购的硬度标样有效期只有一年,到最终用户手里有效期往往只有几个月,不能被用于监测硬度计的长期稳定性;二、因为采购的硬度标样每一块的标称值各不相同,对于有多台硬度计的大型试验机构,难以利用日常监测数据评估不同硬度计之间存在的系统偏差。
技术实现思路
本专利技术所要解决的技术问题是提供一种无时效硬度标样的制作方法,本方法克服了传统硬度标样有效期短的缺陷,可长期有效监测硬度计的长期稳定性,且批量制作的标样具有相同的标称值,方便实施多台硬度计监测值的汇总统计分析。为解决上述技术问题,本专利技术无时效硬度标样的制作方法为选用经终轧温度910℃、卷取温度600℃的熔炼含碳量为0.0014%的超低碳无间隙原子钢钢卷,将所述钢卷切头、切尾和切边加工取得所述钢卷的中间段,采用所述钢卷中间段制得无时效硬度标样。进一步,所述钢卷切头和切尾加工分别切除卷绕的两圈,所述钢卷切边加工为所述钢卷接触传送带的一边切除250mm、另一边切除150mm。由于本专利技术无时效硬度标样的制作方法采用了上述技术方案,即本方法为所述钢卷切头和切尾加工分别切除卷绕的两圈,所述钢卷切 ...
【技术保护点】
一种无时效硬度标样的制作方法,其特征在于:选用经终轧温度910℃、卷取温度600℃的熔炼含碳量为0.0014%的超低碳无间隙原子钢钢卷,将所述钢卷切头、切尾和切边加工取得所述钢卷的中间段,采用所述钢卷中间段制得无时效硬度标样。
【技术特征摘要】
1.一种无时效硬度标样的制作方法,其特征在于:选用经终轧温度910℃、卷取温度600℃的熔炼含碳量为0.0014%的超低碳无间隙原子钢钢卷,将所述钢卷切头、切尾和切边加工取得所述钢卷的中间段,采用所述钢卷中间段制得无时...
【专利技术属性】
技术研发人员:李和平,张益,
申请(专利权)人:上海宝钢工业技术服务有限公司,
类型:发明
国别省市:上海;31