The invention relates to a method for preparing graphene oxide and epoxy resin composite material. The graphene oxide and acetone mixed 1H, ultrasonic treatment, weigh a certain amount of epoxy resin preheating 10min in 80 DEG C water bath; the mixture of graphene oxide and acetone with epoxy resin has been preheated, using a magnetic stirrer in the ventilation cabinet after ultrasonic stirring 0.5h 1H; the mixture is placed in a vacuum the box has been ahead of heating up to 80 DEG C in vacuum 12h; take an appropriate amount of phenolic amine curing agent 31 T mixture and stir 10~20min; by casting the final mixture poured into the mold preheated; at 60 DEG C after curing 2H to remove it. The method of the invention is simple.
【技术实现步骤摘要】
氧化石墨烯和环氧树脂复合材料的制备方法
本专利技术涉及一种氧化石墨烯和环氧树脂复合材料的制备方法。
技术介绍
石墨烯,一颗材料科学领域冉冉升起的新星,具有完美的单层平面结构,单个碳原子被个碳原子包围,其碳原子通过sp2杂化并依次连接,呈正六边形,相邻两个碳原子的间距为0.187nm。石墨烯的性质如下:超高的弹性模量(1000GPa)和强度(50~300GPa),良好的导热性(4.84×103~5.30×103,高的比表面积,良好的电磁性能(电导率达20000S/cm)等。发挥石墨稀优异性能的途径之一是将石墨烯加入到聚合物中制备复合材料,石墨烯作为复合材料的增强体其性能比碳纳米管优异,它的相容性和易官能团化的表面使它与基体能很好地结合。用乙二胺、三乙烯四胺分别对氧化石墨烯进行了表面改性,并以改性后的氧化石墨烯为增强体制备了复合材料。
技术实现思路
本专利技术旨在提出一种氧化石墨烯和环氧树脂复合材料的制备方法。本专利技术的技术方案在于:氧化石墨烯和环氧树脂复合材料的制备方法,采用如下方法:将氧化石墨烯与适量丙酮混合,超声处理1h,称取环氧树脂在水浴中预热;将氧化石墨烯与丙酮的混合物加入已预热的环氧树脂中,在通风柜中使用磁力搅拌器搅拌0.5h后再超声处理1h;将混合物放于已提前加热至80℃的真空箱中抽真空12h;称取固化剂加入混合体系并搅拌10~20min;将最终混合物浇入已预热的模具;在60℃下固化2h后将其取出。所述的模具内表面涂抹甲基硅油,便于脱模。所述的浇铸法中倾斜30°。所述的固化剂为酚醛胺T-31。所述的将最终混合物浇入已预热的模具时采用浇铸法完成。所述 ...
【技术保护点】
氧化石墨烯和环氧树脂复合材料的制备方法,其特征在于:采用如下方法:将氧化石墨烯与适量丙酮混合,超声处理1h,称取环氧树脂在水浴中预热;将氧化石墨烯与丙酮的混合物加入已预热的环氧树脂中,在通风柜中使用磁力搅拌器搅拌0.5h后再超声处理1h;将混合物放于已提前加热至80℃的真空箱中抽真空12h;称取固化剂加入混合体系并搅拌10~20min;将最终混合物浇入已预热的模具;在60℃下固化2h后将其取出。
【技术特征摘要】
1.氧化石墨烯和环氧树脂复合材料的制备方法,其特征在于:采用如下方法:将氧化石墨烯与适量丙酮混合,超声处理1h,称取环氧树脂在水浴中预热;将氧化石墨烯与丙酮的混合物加入已预热的环氧树脂中,在通风柜中使用磁力搅拌器搅拌0.5h后再超声处理1h;将混合物放于已提前加热至80℃的真空箱中抽真空12h;称取固化剂加入混合体系并搅拌10~20min;将最终混合物浇入已预热的模具;在60℃下固化2h后将其取出。2.根据权利要求1所述的氧化石墨烯和环氧树脂复合材料的制备方法,其特征在于:所述的模具...
【专利技术属性】
技术研发人员:王耀斌,
申请(专利权)人:陕西盛迈石油有限公司,
类型:发明
国别省市:陕西,61