一种乙烯基环己基甲醚类液晶化合物及其制备方法技术

本发明专利技术涉及一种乙烯基环己基甲醚类液晶化合物及其制备方法，这些化合物有较大的介电各向异性，有利于提高混合液晶的介电常数，降低阈值电压，从而降低液晶面板的驱动电压，降低功耗，有优良的使用价值。所述液晶化合物的结构如下：上述化合物的结构式中，a、b、c、d、e、g、h、i分别为氢或氟；f为氟。

Vinyl cyclohexyl ether type liquid crystal compound and preparation method thereof

The invention relates to a vinyl cyclohexyl ether liquid crystal compound and a preparation method thereof, these compounds have large dielectric anisotropy, is conducive to the improvement of dielectric constant of liquid crystal mixture, reduce the threshold voltage, thereby reducing the driving voltage of liquid crystal panel, lower power consumption, good use value. The structure of the liquid crystal compound is as follows: A, B, C, D, F, e, G, h and I are hydrogen or fluorine respectively in the formula of the compounds, and fluorine is fluorine.

【技术实现步骤摘要】

本专利技术涉及，属于精细化工和材料化学
。
技术介绍
近年来，液晶应用越来越广泛，乙烯基环己基甲醚类液晶化合物是液晶化合物的重要组成部分，含有此基团的液晶化合物具有粘度低、电荷保持率高，性能优越等特点。专利1W02010095493A1中，涉及到乙烯基环己基甲醚类液晶化合物的制备，如下:

【技术保护点】
一种乙烯基环己基甲醚类液晶化合物，其特征在于，所述乙烯基环己基甲醚类液晶化合物的结构如下：其中，上述化合物的结构式中，a、b、c、d、e、g、h、i分别为氢或氟，f为氟。FDA00003779119000011.jpg

【技术特征摘要】
1.一种乙烯基环己基甲醚类液晶化合物，其特征在于，所述乙烯基环己基甲醚类液晶化合物的结构如下: 2.—种乙烯基环己基甲醚类液晶化合物的制备方法，其特征在于，包括两种合成路线.合成路线1，包括以下步骤:(I)将原料化合物I与原料化合物II在反应溶剂中和碱的催化下经偶联反应得到化合物III ; (2)化合物m与VCMI在反应溶剂中和碱的催化下经醚化反应得到化合物IV ； 其中，所述化合物I的结构式为: 3.根据权利要求2所述乙烯基环己基甲醚类液晶化合物的制备方法，其特征在于，所述合成路线I步骤(1)中碱为氢氧化钾、氢氧化钠、碳酸钾、碳酸钠或碳酸氢钠。4.根据权利要求2所述乙烯基环己基甲醚类液晶化合物的制备方法，其特征在于，所述合成路线I步骤(1)中反应溶剂为醚类溶剂或芳香族溶剂，其中，所述醚类溶剂为四氢呋喃、乙醚、甲基叔丁基醚、二氧六环中一种或几种的混合，所述芳香类溶剂为甲苯、二甲苯中一种或两种的混合。5.根据权利要求2所述乙烯基环己基甲醚类液晶化合物的制备方法，其特征在于，所述合成路线I步骤(1)中偶联反应的反应温度为30~100°C。6.根据权利要求2所述乙烯基环己基甲醚类液晶化合物的制备方法，其特征在于，所述合成路线I步骤(2)中碱为氢氧化钾、氢氧化钠、碳酸钾、碳酸钠或碳酸氢钠。7.根据权利要求2所述乙烯基环己基甲醚类液晶化合物的制备方法，其特征在于，所述合成路线I步骤(2)中反应溶剂为醚类溶剂或芳香族溶剂，其中，所述醚类溶剂为四氢呋喃、乙醚、甲基叔丁基醚、二氧六环中一种或几种的混合，所述芳香类溶剂为甲苯、二甲苯中一种或两种的混合。8.根据权利要求2所述乙烯 基环己基甲醚类液晶化合物的制备方法，其特征在于，所述合成路线I步骤(2)中醚化反应的反应温度为6...

【专利技术属性】
技术研发人员：付海超，葛立权，刘忠文，万君玲，张帆，王斌，韩娜，
申请(专利权)人：烟台万润精细化工股份有限公司，
类型：发明