The present invention provides a method for preparing nano gold nanocomposites with core-shell structure polymer, the method includes two hydrophilic amphiphilic polymer dissolved amino containing micelles in water; and chloroauric acid solution which was prepared with core-shell structure polymer / gold nanoparticles composite nano material steps. The invention also provides a core-shell structure polymer / nano gold composite nano material prepared by the method, and a product made of the composite nanometer material. The method of the invention has the advantages of simple operation, mild reaction, low cost and environmental friendliness; the composite nanometer material of the invention has good stability, good dispersivity, uniform particle size and no toxic side effects.
【技术实现步骤摘要】
核壳结构聚合物/纳米金复合纳米材料及其制备方法和应用
本专利技术涉及复合材料领域。具体地说，本专利技术涉及核壳结构聚合物/纳米金复合纳米材料、及其制备方法和应用。
技术介绍
纳米金具有独特的光、热、电及化学方面的性能，在催化、光电器件和生物医学等领域的潜在应用引起了众多研究人员的关注。聚合物作为重要的功能材料，已经在各个领域得到广泛应用。将聚合物与纳米金复合是开发新型功能复合材料的有效途径之一。要形成聚合物为核、纳米金为壳的核壳结构，一般的合成方法至少需要3步。首先，通过乳化法、薄膜水化法等方法将聚合物材料制备成纳米材料；其次，采用水相中化学还原法制备纳米金；最后，将纳米材料与纳米金混合，通过静电吸附或者聚合物所带巯基与纳米金相互作用形成核壳结构聚合物/纳米金复合纳米材料。现有技术中制备核壳结构聚合物/纳米金复合纳米材料的方法的合成过程繁琐，容易引入乳化剂、有机溶剂、还原剂、稳定剂等杂质，从而不利于复合纳米材料的下一步应用。因此，本领域急需操作简便、反应温和、成本低廉的制备核壳结构聚合物/纳米金复合纳米材料的方法，以及具备稳定性好、分散性好、粒径均一且无...
【技术保护点】
一种制备核壳结构聚合物/纳米金复合纳米材料的方法，其特征在于，所述方法包括以下步骤：(1)将亲水端含氨基的两亲性聚合物溶解于水中形成胶束；(2)将氯金酸溶液加入其中，反应制得核壳结构聚合物/纳米金复合纳米材料。
【技术特征摘要】
1.一种制备核壳结构聚合物/纳米金复合纳米材料的方法，其特征在于，所述方法包括以下步骤: (1)将亲水端含氨基的两亲性聚合物溶解于水中形成胶束； (2)将氯金酸溶液加入其中，反应制得核壳结构聚合物/纳米金复合纳米材料。2.如权利要求1所述的方法，其特征在于，所述亲水端含氨基的两亲性聚合物选自下组中的至少一种:普朗尼克-壳聚糖、普朗尼克-壳寡糖、普朗尼克-氨基酸、普朗尼克-多肽和普朗尼克-聚亚乙基亚胺。3.如权利要求1或2所述的方法，其特征在于，所述氯金酸和亲水端含氨基的两亲性聚合物的摩尔质量比为I: (0.001-1000);优选地,所述摩尔质量比为1: (0.01-500);更优选地，所述摩尔质量比为1: (0.05-100) O4.一种核壳结构聚合物/纳米金复合纳米材料，其特征在于，所述材料具有聚合物为核、纳米金为壳的核壳结...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。