The invention relates to a high-speed milling corner panel parts processing method, which is characterized in that the following steps: 1) panel angle R is less than or equal to 6 parts design; 2) to complete the panel parts cavity rough milling preparation; 3) cutter selection and cavity radius corresponding to the angle in milling to, will be used for fine milling cutter profile at the corner point as a benchmark, at a distance of 3 ~ 5mm point outward position as the breakthrough point angle precision milling, the angle of about 1 degrees to 3 degrees; 4) of large depth of cut milling in shape with milling cutter in. The method not only improves the surface accuracy of the machined parts, but also saves the processing time and improves the work efficiency.
【技术实现步骤摘要】
本专利技术涉及一种，用于在数控加工中对典型 槽腔、相对小转角结构零件的高效加工方法。
技术介绍
目前某机型飞机壁板零件材料规格为δ 45 X 3800 X 1200，材料牌号为2D70 Τ351。 此零件槽腔较多，约为13排槽，每排约为12—14个槽腔，约共计200槽腔。原工艺流程为 粗铣外形一粗铣内形一精铣筋条高一精铣腹板一精铣内形一精铣转角一精铣外形，加工转 角的主要工艺是用铣刀以3mm为一层精铣零件内形，然后用铣刀进行精铣零件转角，该转 角加工工艺不仅存在零件表面粗糙度一般，而且局部可能还存在凹刀现象，甚至出现刀具 易断的现象。
技术实现思路
本专利技术要解决的技术问题是提供一种，该方 法不仅提高了加工零件的表面精度，而且节省了加工时间，提高了工作效率。为解决以上问题，本专利技术的具体技术方案如下一种高速铣加工壁板类零件转角 加工方法，其特征在于如下步骤1)壁板类零件设计的转角R彡6mm ；2)完成壁板类零件槽腔粗铣加工的准备工作；3)选择与槽腔转角半径对应的铣刀进行转角精铣，以将用于精铣内形的刀具在 转角的切点为基准，在距离切点向外3 5mm的位置为转角精铣...
【技术保护点】
一种高速铣加工壁板类零件转角加工方法，其特征在于如下步骤：１）壁板类零件设计的转角Ｒ≤６ｍｍ；２）完成壁板类零件槽腔粗铣加工的准备工作，侧壁留有１～１．５ｍｍ的加工余量；３）选择与槽腔转角半径对应的铣刀进行转角精铣，以将用于精铣内形的刀具在转角的切点为基准，在距离切点向外３～５ｍｍ的位置为转角精铣刀的切入点，切入角度约为１°～３°；４）用精铣内形铣刀进行大切深精铣内形。
【技术特征摘要】
【专利技术属性】
技术研发人员：李伟兴，初宏震，
申请(专利权)人：沈阳飞机工业集团有限公司，
类型：发明
国别省市：89
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。