一种钴基合金粉及其在激光修复核电海水泵轴上的应用制造技术

本发明专利技术公开了一种钴基合金粉及其在激光修复核电海水泵轴上的应用，钴基合金粉的组份和重量百分比为：C:0.85～1.10％;Cr:21～23％;Fr:≤1.0％;Ni:11.0～12.0％;W:8～10％;Ti:0.2～0.4％;P:≤0.030％;S:≤0.030％，其余为钴;合金粉目数：130～300。本发明专利技术既增强了材料的抗海水腐蚀性，也提高了抗磨强度，又保证了激光融覆过程中无裂纹产生。修复处的材料不仅耐海水腐蚀、耐磨强度也非常好，与激光工艺结合达到了最佳的冶金结合状态，无裂纹、无夹杂，硬度在HRC50左右，提高了部件的使用寿命。?

Cobalt based alloy powder and its application in laser repairing nuclear power sea water pump shaft

The invention discloses a cobalt base alloy powder and its application in laser repair of nuclear seawater pump shaft, cobalt based alloy powder composition and weight percentage: C:0.85 ~ 1.10%; Cr:21 ~ 23%; Fr: = 1%; Ni:11.0 ~ 12%; W:8 ~ 10%; Ti:0.2 ~ 0.4%; P: = 0.030%; S: = 0.030%, for the rest of the cobalt alloy powder; mesh: 130 ~ 300. The invention not only enhances the seawater corrosion resistance of the material, but also improves the abrasion resistance strength, and ensures that no crack occurs during the laser cladding process. Repair the material not only seawater corrosion resistance, abrasion resistance is also very good, and the laser technique combined with the best metallurgical bonding state, without cracks and inclusions, the hardness of about HRC50, to improve the service life of the components. ?

【技术实现步骤摘要】

本专利技术涉及一种合金材料，具体是一种钴基合金粉及其在激光修复核电海水泵轴上的应用。
技术介绍
现有核电站因需要水量较大，一般大多建在海边或湖边，其中水泵是提取海水或 湖水的重要部件之一。海水泵技术要求较高，其特性要求能够耐磨损、耐海水腐蚀、耐泥沙 冲刷，现大多使用进口水泵。水泵是由壳体、叶轮、传动轴、密封器件等组成，由电动设备带 动传动轴转动，使装在传动轴上的叶轮旋转，在壳体及密封件的封闭下，水从进水口被吸入 从出水口被高压喷出，如有出现密封不好状态，水会从泵体内溢出，造成水泵内压力减少， 达不到规定的供水要求。经常出现的问题是水泵密封处腐蚀和磨损，水泵传动轴与壳体的 密封是水泵重要密封处之一，传动轴与壳体、密封圈是接触式密封，密封圈容易更换，且成 本较低，但传动轴的更换较难而且成本较高。因核电机组投料运行周期较长(一般为12 18个月)，而且要求水泵在整个周期内毫无故障的不停机运行，故传动轴的修复显得较为 重要，用其他方法修复不是结合强度不够，就是易造成基材组织损伤，易出现剥落或断轴现 象。如果采用激光修复可避免以上事件发生，但是对修复所用的合金料要求非常高，既要求 合金料的本文档来自技高网...

【技术保护点】
一种钴基合金粉，其特征在于组份和重量百分比为：Ｃ：０．８５～１．１０％；Ｃｒ：２１～２３％；Ｆｒ：≤１．０％；Ｎｉ：１１．０～１２．０％；Ｗ：８～１０％；Ｔｉ：０．２～０．４％；Ｐ：≤０．０３０％；Ｓ：≤０．０３０％，其余为钴；　合金粉目数：１３０～３００。

【技术特征摘要】

【专利技术属性】
技术研发人员：李光伟，梁栋，
申请(专利权)人：江苏斯普瑞表面处理技术有限公司，
类型：发明
国别省市：32