The invention provides a preparation method of porous graphene material. (1) the nano particles of metal oxide dispersed in the solvent; (2) the soluble salt and polymer graphite catalyst steps (1) the product obtained in uniform mixing; (3) the step (2) product heating vacuum to remove the solvent; (4) the step (3) the product in an inert atmosphere at 500-1000 deg.c for 0.5-400min heat treatment, cooling after collecting a solid product; (5) with dilute acid treatment of solid product catalyst and metal oxide nano particles removed, namely porous graphene materials. The porous graphene material prepared by the method of the invention has low oxygen content, high graphitization degree and hole diameter larger than 2nm in the graphite flake layer. The preparation method is simple, the raw materials are easy to obtain, and can be prepared in batches and easy to realize industrial production.
【技术实现步骤摘要】
本专利技术涉及的是一种纳米材料的制备方法，具体涉及一种批量制备多孔石墨烯的 方法。
技术介绍
石墨烯材料是由单层石墨组成的纳米级石墨材料，由于具有优异的导电性、导 热性及力学性能，在纳米器件、导热、导电及储能领域有着巨大的潜在应用价值，石墨烯 材料的理论比表面积高达^K)0m2/g，具有突出的导热性能(3000W/(m*K))和力学性能 (1060GPa)，以及室温下高速的电子迁移率(15000cm2/(V · s))。多孔石墨烯是在石墨烯的 片层中通过物理或化学的方法制造一些具有纳米尺寸的孔洞，这种结构使得石墨烯在做为 能源、催化或者吸附材料时，不仅具有很高的比表面积，同时还有很好的传质效应，充分发 挥这种二维纳米片层材料的优势，目前关于多孔石墨烯的制备还少有报道。
技术实现思路
本专利技术的目的在于提供一种能制备出含氧量低、石墨化度高、在石墨烯片层分布 直径大于2nm的孔洞的多孔石墨烯材料，而且原料成本低、工艺简单、易于批量生产的多孔 石墨烯材料的制备方法。本专利技术的目的是这样实现的(1)将金属氧化物的纳米颗粒分散在溶剂中；(2)将石墨化催化剂的可溶性盐及聚合...
【技术保护点】
１．一种多孔石墨烯材料的制备方法，其特征是：（１）将金属氧化物的纳米颗粒分散在溶剂中；（２）将石墨化催化剂的可溶性盐及聚合物加入步骤（１）得到的产物中，均匀混合；（３）将步骤（２）得到的产物加热抽真空去除溶剂；（４）将步骤（３）所得产物于惰性气氛下在５００－１０００℃温度下热处理０．５－４００ｍｉｎ，冷却后收集固体产物；（５）用稀酸处理固体产物将催化剂以及金属氧化物纳米颗粒溶解除去，即得多孔石墨烯材料。
【技术特征摘要】
【专利技术属性】
技术研发人员：范壮军，魏彤，闫俊，赵乾坤，
申请(专利权)人：哈尔滨工程大学，
类型：发明
国别省市：93