The invention relates to a method for preparing graphene by heating an organic solvent suspension of graphite oxide, relating to a method for preparing graphene by chemical dispersion, belonging to the technical field of preparation of graphene. Includes the following steps: (1) the graphite oxide in polar organic solvent, ultrasonic ranging from 2 to 5 hours, to suspension concentration is 0.01 ~ 10g/L; (2) the step (1) of the suspension was heated for 4 to 24 hours, until the suspension became black, and all or part of condensation; (3) the step (2) black suspension filtration, the removal of polar organic solvent; (4) to step (3) of the filter cake drops into the organic electrolyte solution and filtered, a black paste is applied directly to the detention body or directly use; drying steps (3) the cake to graphene materials. Process and apparatus of the present invention relates to a simple process, easy mass production, resulting in low price, no water and high conductivity of graphene materials.
【技术实现步骤摘要】
本专利技术涉及一种化学分散法制备石墨烯的方法，属于石墨烯制备
技术介绍
本专利技术涉及一种直接加热氧化石墨在有机溶剂中的悬浮液得到石墨烯材料的方法。利用氧化石墨在某些有机溶剂中的良好分散性以及这些有机溶剂的相对较高沸点及较低蒸汽压，可直接加热氧化石墨的悬浮液，从而有效去除氧化石墨上的含氧官能团。这样得到的完全干燥(无水)的石墨烯材料在有机溶剂中有一定程度的分散性，可直接用于某些对水分高度敏感的器件，比如超级电容器或者锂离子电池中。此外，也可以进一步去除有机溶剂，得到石墨烯粉状或者纸状材料。
技术介绍
石墨烯，英文名Graphene，是碳原子按照六角排列而成的二维晶格结构。作为单层碳原子平面材料，石墨烯可以通过剥离石墨材料而得到。这种石墨晶体薄膜自2004年被曼彻斯特大学的科学家发现之后，石墨烯就成为科学界和工业界关注的焦点。石墨烯的厚度只有0. 335纳米，不仅是已知材料中最薄的一种，还非常牢固坚硬；作为单质，它在室温下传递电子的速度比已知所有的导体和半导体都快(石墨烯中电子的迁移速度达到了光速的1/300)。由于石墨烯的特殊原子结构，其中载流子(电子和...
【技术保护点】
１．加热氧化石墨的有机溶剂悬浮液制备石墨烯的方法，其特征在于：包括如下步骤，（１）、将氧化石墨置于极性有机溶剂中，超声２～５小时，得悬浮液，质量浓度为０．０１～１０ｇ／Ｌ；（２）、将步骤（１）的悬浮液加热４～２４小时，至悬浮液变成黑色，同时有部分或者全部凝聚；（３）、将步骤（２）的黑色悬浮液过滤，去除极性有机溶剂；（４）、向步骤（３）所得滤饼中滴入有机电解质溶液并抽滤，得黑色浆状物并直接涂布于羁留体使用；或者直接干燥步骤（３）所得滤饼，得石墨烯材料。
【技术特征摘要】
【专利技术属性】
技术研发人员：瞿研，
申请(专利权)人：无锡第六元素高科技发展有限公司，
类型：发明
国别省市：32