The invention belongs to the technical field of hot melt adhesive, in particular to a strengthening type heat shrinkable sleeve hot melt adhesive and a preparation method thereof. The first technical problem to be solved is to provide an improved heat shrinkable sleeve hot melt adhesive, wherein the strengthening type heat shrinkable sleeve, hot melt adhesive is sealed, and the corrosion prevention effect is good. The invention relates to an improved heat shrinkable sleeve hot-melt adhesive which comprises 3~20 components with the following weight: terpene resin 20~50 parts, EVA 35~75 parts, antioxidant 0~6 parts and filling parts. The present invention reinforced heat shrinkable hot-melt adhesive has high temperature resistance, and high peeling strength, peel strength of PE PE is greater than 182N/cm and PE on epoxy primer peel strength greater than 205N/cm, can meet the requirements of oil and natural gas, heat sealing and anticorrosion requirements.
【技术实现步骤摘要】
本专利技术属于热熔胶
，特别涉及。
技术介绍
随着环境要求的提高，管道密封和防腐成为社会日益重视的问题。由于传统用普通型热缩套管穿越有明显缺点，在穿越拖拉工程中容易拉断。而加强型热缩套管采用两边聚乙烯中间纤维网，强度高、柔韧性好，碰撞和变形不会开裂。聚乙烯是低表面难粘的材料，目前已经有两种穿越方法，这些方法各有缺点。上述连接方法可分为普通型热缩套管和热缩带穿越，在穿越拖拉工程中容易拉断，需要重新再来，那样就给施工带来不必要的麻烦，施工难度增加，相应的成本也增加。因此很需要一种施工方便、性能可靠、成本低的穿越连接方法。加强型热缩套管内层胶粘剂是由几种材料组成，该胶粘剂粘接强度高，适用于钢管、塑料管的粘接。通常是将石油树脂、EVA、浙青混合成为热熔胶粘剂，但使用时热缩套 (带)PE对PE剥离强度70N/cm、PE对FBE剥离强度70N/cm，因此无法满足管道穿越要求的粘接强度。
技术实现思路
本专利技术所要解决的第一个技术问题是提供一种加强型热缩套管热熔胶粘剂，该加强型热缩套管热熔胶粘剂密封、防腐效果好。本专利技术加强型热缩套管热熔胶粘剂由下列重量份的组份组成萜烯...
【技术保护点】
１．加强型热缩套管热熔胶粘剂，其特征在于：由下列重量份的组份组成：萜烯树脂２０～５０份、ＥＶＡ ３５～７５份、抗氧剂０～６份和填料３～２０份。
【技术特征摘要】
【专利技术属性】
技术研发人员：张玉根，青云凤，彭忠全，
申请(专利权)人：成都市双流川双热缩制品有限公司，
类型：发明
国别省市：90