The invention discloses a method for oil shale residue, preparation of 4A molecular sieve comprises: crushing; the mixture; the calcination; the aging; and the filtering step of crystallization. The invention is a kind of alkali calcination method, mainly for oil shale waste in mostly quartz form, low activity, it is difficult to react with alkali liquid, can make alkali synthesis and slag in the molten state, thereby generating a 4A molecular sieve. The method can make full use of oil shale waste, improve the utilization rate, increase the economic benefit, and avoid the accumulation of a large number of waste residue, reduce the amount of land, reduce the environmental pollution. The method has the advantages of simple process, small investment and low cost, and is a promising industrial method for fine chemical and comprehensive utilization of oil shale waste residue.
【技术实现步骤摘要】
本专利技术涉及一种用油页岩废渣制备4A分子筛的方法。
技术介绍
随着石油资源的日益减少，一些诸如油页岩等替代能源越来越受到重视。油页岩能源 的主要利用方式是提炼页岩油。但由于油页岩中灰分所占比重达80%以上，油页岩炼化后 会排放大量的油页岩废渣。以抚顺为例，每年排放的油页岩废渣约500万吨左右。大量的 废渣长时间堆放在露天环境中，经历降水、淋滤、风化和自燃作用，会发生一系列的物理、化 学反应，产生了大量的污染物并向外排放，造成了周围地区空气、土壤、地下水严重污染。油 页岩废渣中含有5(T70%Si02，1(T25%A1203。SiO2和Al2O3总和占成分的70%以上，正是制备 4Α分子筛的主要原料，利用油页岩废渣制备4Α分子筛使其变废为宝，是一种行之有效的办 法。4Α分子筛是一种碱金属硅铝酸盐，能吸附水、NH3、H2S、二氧化硫、二氧化碳、C2H50H、C2H6、 C2H4等临界直径不大于4A的分子。广泛应用于气体、液体的干燥，也可用于某些气体或液 体的精制和提纯，如氩气的制取。
技术实现思路
本专利技术的目的是提供一种用油页岩废渣制备4A分子筛的方法，采用该方法...
【技术保护点】
１．一种用油页岩废渣制备４Ａ分子筛的方法，包括如下步骤：①将油页岩废渣破碎至２００目；②按照ＳｉＯ２／Ａｌ２Ｏ３摩尔比为１－６：１，Ｎａ２Ｏ／ＳｉＯ２摩尔比为２－６：１，将油页岩废渣、氧化铝粉和氢氧化钠混合均匀，破碎；③将步骤②所得混合料在５００℃－１１００℃温度下煅烧１－５小时；④将步骤③所得熟料破碎至２００目；⑤按照水／Ｎａ２Ｏ摩尔比为２５－７５：１，将步骤④所得熟料加入水中；⑥在２０℃－６０℃温度下，陈化５－３６小时；⑦升高温度至６０℃－１２０℃，晶化６－１６小时；⑧过滤即得４Ａ分子筛产品。
【技术特征摘要】
【专利技术属性】
技术研发人员：韩放，张振庭，鲍明福，高健，赵鑫，姚兴光，
申请(专利权)人：抚顺矿业集团有限责任公司，
类型：发明
国别省市：21
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。