The invention relates to a vanadium redox flow battery electrode modification method of graphite felt the first processing of graphite felt using air oxidation method, and then use hydrogen peroxide or Fenton reagent modification of graphite felt after air oxidation treatment, which comprises the following steps: air oxidation treatment A.: graphite felt in the air clean the heating device, heating, thermal oxidation in air, oxidation treatment, heating device in natural cooling to room temperature; then the cooled graphite felt clean; hydrogen peroxide or B. modification agent Fenton: clean the graphite felt in hydrogen peroxide solution and Fenton reagent in the modification, the modified graphite felt; graphite felt surface residue processing C. by hydrogen peroxide solution or Fenton reagent stone using distilled water Ink felt was removed by removing the hydrogen peroxide or Fenton reagent on the graphite felt surface. The utility model has the advantages that the operation is simple, the cost is low, and the environment is friendly.
【技术实现步骤摘要】
本专利技术属于电池电极制造
，涉及石墨毡的表面改性处理方法，特别是一 种全钒液流电池电极用石墨毡的改性方法，其主要用于全钒液流电池。
技术介绍
全钒液流电池是一种新型高效的绿色环保二次电池。它在生产和使用过程中均不 会产生对人体及环境有害的物质。钒电池以钒离子溶液为正负极活性物质，与其他液流电 池一样没有固态反应，不发生电极物质结构形态的变化。其价格便宜、使用寿命长、可靠性 高、操作和维护费用低。据有关资料介绍，石墨毡，特别是聚丙烯腈基石墨毡电极，因其具有 较宽的工作电压范围、稳定性好、表面积高等优点，而广泛应用于全钒液流电池中，通过对 其表面附着金属离子和氧化等方法能大大提高其化学活性。常用的石墨毡氧化改性的方法，有空气氧化法、强酸氧化法与电化学氧化法。其 中，空气氧化法的操作弹性小，氧化反应不容易控制；2005年8月发表在中国有色金属学报 上的“石墨毡电极的化学修饰及其在酸性钒溶液中的电化学行为”介绍的技术方法，是采用 强酸氧化法对石墨毡进行处理，使用强酸是十分危险，有很大的安全隐患，这种技术方法应 用于工业化生产，其难度大，且会导致碳纤维表面剧烈反应...
【技术保护点】
１．一种全钒液流电池电极用石墨毡的改性方法，采用空气氧化法，其特征在于：首先使用空气氧化法对石墨毡进行处理，然后再使用过氧化氢或芬顿试剂对经过空气氧化法处理的石墨毡进行改性，包括以下步骤：ａ．空气氧化处理：将清洗干净的石墨毡置于加热装置中，进行加热，在热空气环境中进行氧化处理，氧化处理后，在加热装置中自然冷却至室温；再将冷却后的石墨毡清洗干净；ｂ．过氧化氢或芬顿试剂改性处理：将清洗干净的石墨毡置于过氧化氢溶液或芬顿试剂中进行改性处理，得到改性石墨毡；ｃ．石墨毡表面的残留物处理：使用蒸馏水对经过过氧化氢溶液或芬顿试剂处理的石墨毡进行清洗，除去石墨毡表面残留的过氧化氢或芬顿试剂。
【技术特征摘要】
【专利技术属性】
技术研发人员：李爱魁，杜涛，杜忠东，陈家宏，陈轩恕，罗传仙，刘飞，张杰，
申请(专利权)人：国网电力科学研究院武汉南瑞有限责任公司，国网电力科学研究院，
类型：发明
国别省市：83
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。