A resistance welding method, by using a pair of electrode tip (34, 36) to specify the welding pressure clamped on the workpiece (60, 62) and the electrode tip (34, 36) to (60, 62) the supply of welding current and the workpiece (60, 62) for resistance welding, the method includes the following steps: detecting the workpiece (60, 62) in the nugget (64) along the electrode tip (34, 36) during the clamping of the workpiece (60, 62) expansion rate of change along the direction of change; whether the detected judgment is less than the threshold; and after less than the threshold change the judgment of the detected, gradually increase the flow through the workpiece (60, 62) of the welding current.
【技术实现步骤摘要】
本专利技术涉及用于通过控制施加至工件的焊接压力和通过工件的焊接电流有效地 电阻焊接工件的。
技术介绍
如在日本特许专利公开No. 04-178274中披露的那样，迄今已经知道了一种关于 电阻焊接工艺的技术概念，其中当与将被焊接的工件保持接触的电极尖端被激励时，大电 流最初供给至工件，随后在熔核开始形成在工件中时，向工件供给降低的电流，随后在电阻 焊接工艺的中间阶段之后向工件供给逐渐增加的电流，由此在工件中形成大体积的熔核， 而不引起实质的爆裂。然而，根据在日本特许专利公开No. 04-178274中披露的技术概念，关于电流应当 逐渐增加的时间点是不清楚。取决于电流开始逐渐增加的时间，会发生倾向阻止熔核生长 的爆裂。
技术实现思路
本专利技术的目标是提供一种，其最小化爆裂的发生频率，以促进熔核 的生长。为了实现上述目标，根据本专利技术，提供了 一种方法，其通过采用一对电极尖端以指 定焊接压力夹紧一对工件并通过电极尖端向工件供给焊接电流而对工件进行电阻焊接，该 方法包括下述步骤检测在工件中产生的熔核沿着电极尖端夹紧其间的工件所沿的方向的 膨胀量的变化；判断检测到的变化是...
【技术保护点】
１．一种电阻焊接一对工件（６０，６２）的方法，其通过采用一对电极尖端（３４，３６）以指定焊接压力夹紧一对工件（６０，６２）并通过电极尖端（３４，３６）向工件（６０，６２）供给焊接电流，该方法包括下述步骤：检测在工件（６０，６２）中产生的熔核（６４）沿着电极尖端（３４，３６）夹紧其间的工件（６０，６２）所沿的方向的膨胀量的变化；判断检测到的变化是否小于阈值；以及在判断检测到的变化小于所述阈值之后，逐渐增加流过工件（６０，６２）的焊接电流。
【技术特征摘要】
...
【专利技术属性】
技术研发人员：长谷川荣作，青木裕志，金子贡，牧田琢，武石克己，
申请(专利权)人：本田技研工业株式会社，
类型：发明
国别省市：JP
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。