结晶器模具润滑油制造技术

本发明专利技术是关于一种结晶器模具润滑油，以重量百分含量计算，其包括：聚烯烃：９０－９８％；油酸三羟酯：１－９％；酚型抗氧化剂：０．１－４％；以及芳胺型抗氧化剂：０．２－４％；上述各个物质的总和为１００％。优选的，聚烯烃为合成基础油ＰＡＯ６；油酸三羟酯为油酸三羟丙烷酯；酚型抗氧化剂为Ｌ１１５；芳胺型抗氧化剂为Ｌ０１。该润滑油具有适合的渗透性能，具有良好的助滑减摩性能，同时该润滑油不结焦、不生烟、无毒、无臭、流动性好等特点，满足扁锭铸造生产线的环保要求。

Mould lubricant

The present invention relates to a mould die lubricating oil, according to the weight percentage calculation, including: Polyolefin: 90 - 98%; three: 1 - hydroxy oleic acid ester 9%; phenolic antioxidants: 0.1 - 4%; and aromatic amine type antioxidants: 0.2 - 4%; the sum of all material is 100%. Preferred polyolefin is synthetic base oil PAO6; oleic acid three hydroxy ester is oleic acid three propane ester; phenolic type antioxidant is L115; aromatic amine type antioxidant is L01. The lubricating oil has suitable permeability, good slip friction reducing property, and the lubricating oil coking, no smoke, non-toxic, odorless, good fluidity and other characteristics, flat ingot casting production line to meet the requirements of environmental protection.

【技术实现步骤摘要】

本专利技术涉及一种冶金技术的润滑油，特别是涉及一种铝合金铸造技术 中应用的结晶器模具润滑油。
技术介绍
美国Wagstaff LHC低液位铸造技术，在铝合金生产领域的发展起到了 良好的推动作用，产品质量和生产效率得到了提高，但是部分高消耗备品、 备件和材料，需要进口加以补充，而进口件价格昂贵，且购买周期长，不但 使生产成本增加，还可能使生产的稳定性和连续性受到影响，还将使新产 品、新工艺的开发运用受到极大的制约。有色金属特别是铝及其合金的铸造用润滑油，多是压铸和重力浇铸模 具润滑油，其通常采用水基压铸涂料(硅油、植物油等)，而重力浇铸采用 石墨乳、立方氮化硼乳液或油性石墨膏等，但没有合成结晶器模具油的文献。结晶器模具润滑油主要是起隔离作用，即隔离模具和液态金属，防止 铝合金粘附和沉积在模具上，因此对高温稳定性和抗氧化性要求极高。现 有的结晶器模具润滑油通常采用矿物油或动物油脂，这类润滑油品有很多 缺点，如闪点低、生烟多、气味大、消耗大、金属表面光亮度差等。由此可见，上述现有的结晶器模具润滑油仍存在有不便与缺陷，而亟 待加以进一步改进。有鉴于上述现有的结晶器模具润滑油存在的缺陷，本专本文档来自技高网...

【技术保护点】
一种结晶器模具润滑油，其特征在于以重量百分含量计算，包括：　聚烯烃：９０－９８％；　油酸三羟酯：１－９％；　酚型抗氧化剂：０．１－４％；以及　芳胺型抗氧化剂：０．２－４％；　上述各个物质的总和为１００％。