一种铝合金材料表面纳米化处理方法技术

本发明专利技术涉及一种铝合金材料表面纳米化处理方法，其步骤如下：首先将超声波表面强化处理装置垂直对准处理工件表面；然后接通电源，打开超声波表面强化处理装置，使所述超声波表面强化处理装置针对待处理工件机械动力密排等距，等速行走，对待处理工件沿轴向等速密排处理。本发明专利技术的铝合金材料表面纳米化处理方法采用塑形变形方法和相当大的变形速度处理工件表面，使待处理工件的疲劳强度，腐蚀抗力，屈服和断裂点，磨损阻抗，光的折射系数增加，并且使材料表面致密化，尺寸减小，密度增加。

Surface nanocrystallization treatment method for aluminium alloy material

The invention relates to a Aluminum Alloy surface nanocrystallization method, the steps are as follows: first, the processing device of vertical alignment processing of workpiece surface ultrasonic surface; and then connect the power, open the surface strengthening treatment device of ultrasonic, the ultrasonic processing device for surface strengthening treatment closepacked equidistant workpiece mechanical power walking speed, treat the isokinetic treatment workpiece densely along the axial direction. Aluminum Alloy the nanometer material surface treatment method using plastic deformation method and the deformation speed in dealing with the surface of the workpiece, the workpiece processing to fatigue strength, corrosion resistance, yield and fracture, wear resistance, increase of refractive index of light, and the material surface densification, size, density increased.

【技术实现步骤摘要】

本专利技术涉及，特别涉及一种用于铝合金材 料表面处理的超声波处理方法。
技术介绍
金属材料的表面纳米化有各种各样的方法。利用严重塑性变形方法可使金属材 料的微米晶粒细化形成超细晶或纳米晶，这类方法包括等通道转角挤压、高压扭转(HPT)、表面机械研磨(SMAT)和高能球磨(服BM)等。其中表面机械研磨和高能球磨 属于高应变率"& 〉103 /s)的塑性变形方法。表面机械研磨(SMAT)是近几年发展起来的一项新的表面纳米化技术。研究结果 表明，在SMAT中由于受弹丸的高速、多方位重复冲击，材料表层的粗晶组织通过产 生强烈的高应变率塑性变形而逐渐细化至纳米量级(10 — 30 rnn)。 大量的TEM观察结果表明，SMAT在原始晶粒中引入了大量的位错、界面(晶界)等晶 体缺陷，从而使晶粒发生破碎，其破碎程度取决于应变和应变率的大小。随着材料 表层深度的减小，应变和应变率逐渐增加，从基体到表面可依次产生形变粗晶层、 细化结构层和纳米结构层(厚度为10 — 50 um)。在形变粗晶层中，材料的粗晶组织通常可产生位错、层错、孪晶等缺陷，以此 来协调塑性应变；在细化结构层中，应变和应变本文档来自技高网...

【技术保护点】
一种铝合金材料表面纳米化处理方法，其步骤如下：　首先将超声波表面强化处理装置垂直对准处理工件表面；然后接通电源，打开超声波表面强化处理装置，使所述超声波表面强化处理装置针对待处理工件机械动力密排等距，等速行走，对待处理工件沿轴向等速密 排处理。

【技术特征摘要】

【专利技术属性】
技术研发人员：朱其芳，孙泽明，王福生，张东晖，朱宝宏，熊柏青，
申请(专利权)人：北京有色金属研究总院，
类型：发明
国别省市：11[中国|北京]