A method of reclaiming alumina and sodium oxide in Bayer red mud includes red mud leaching reaction in 3070wt%NaOH solution, alkali solution and red mud weight ratio of 4 to 1 to 8 to 1 DEG C, leaching temperature 180250, leaching time 0.25h, leaching pressure 0.31.8MPa, filter containing sodium lye and dealumination of red mud the crystallization of aluminum acid sodium lye; 50 - 100 DEG C to hydrated sodium aluminate crystal and the crystallization solution, crystallization mother liquor circulation for the leaching reaction; sodium aluminate hydrate coarse dissolved in water return to Bayer production, the kind of desilication and calcined alumina; removing aluminum in red mud water and dealumiumazation red mud weight calcium oxide 5 - 20%, solid-liquid ratio of 6: 1 to 10: 1100 to 180 DEG C and sodium, The red mud after sodium removal is used for cement production, and NaOH solution is used for leaching reaction. The dissolution temperature and pressure of this method are lower and the dissolution rate of alumina is up to 90%.
【技术实现步骤摘要】
本专利技术涉及氧化铝和氧化钠的生产方法领域，特别涉及一种低温低压回 收拜耳法赤泥中氧化铝和氧化钠的方法。
技术介绍
目前，全世界基础产业均面临世界性能源短缺，资源日益匮乏，环境保 护越来越受到人们的关注，对于氧化铝工业，这些挑战越加尖锐。我国氧化铝生产主要以难溶的一水硬铝石型铝土矿为原料，据统计A/S>10的矿石只占10°/。， A/S为7-10的矿石占20%，而A/S为4-7的矿石占 60%以上，高铝、高硅、低铝硅比是我国铝土矿的重要特色。用纯的拜耳法 处理A/S在4-7的一水硬铝石型铝土矿时，氧化铝回收率j氐，导致资源利用 率低，对氧化铝生产过程的经济社会效益有严重的影响。为了提高氧化铝的 回收率，前苏联和我国长期致力于采用拜耳烧结联合法技术研究，取得了重 大成就。但实践证明，联合法生产流程在一定程度上存在能耗高，生产流程 复杂，生产效率不高等弊端。现有回收赤泥中氧化铝生产方法主要是烧结法，该方法以拜耳法赤泥和 碳酸钠混合，在1000。C以上进行烧结，得到固体铝酸钠烧结产物，然后用稀 碱溶出便得到铝酸钠溶液，往溶液中通入二氧化碳即得到氩氧化铝，残留在 ...
【技术保护点】
一种回收拜尔法赤泥中氧化铝和氧化钠的方法，其步骤如下： １）将拜耳法赤泥在重量百分比浓度为３０－７０％的ＮａＯＨ水溶液中进行浸出反应，所述的碱溶液与拜耳法赤泥的重量份配比为４∶１～８∶１，浸出反应的浸出温度为１８０－２５０℃，浸出反应 时间为０．２－５小时，浸出反应完成后保温过滤得到含铝酸钠的碱液和脱铝赤泥； ２）将步骤１）得到的含铝酸钠的碱液在５０－１００℃下进行结晶，过滤得到水合铝酸钠粗晶及其结晶母液，结晶母液循环用于步骤１）的浸出反应；得到的水合铝酸钠粗晶用水 溶解后，返回拜尔法生产主流程，经脱硅种分操作后得氢氧化铝，再经煅烧后，得到氧化铝； ３）...
【技术特征摘要】
【专利技术属性】
技术研发人员：郑诗礼，孙旺，张亦飞，钟莉，张懿，
申请(专利权)人：中国科学院过程工程研究所，
类型：发明
国别省市：11[中国|北京]