The invention relates to a preparation method of gold nanoparticles modified Zinc Oxide for treating sewage in environmental protection. It includes the following steps: A, the zinc salt solution and six methyl four amine solution mixing, zinc salt solution and six methyl amine solution of four molar ratio of 1: 1 to 4; the mixed solution of A and B in zinc salt solution and six methyl four amine solution consisting of adding salt the solution and stirring, gold salt solution with zinc salt solution the molar ratio of 1: 100 to 1000; C, B mixture composed of zinc salt solution, six methyl four amine solution and salt solution to the reaction temperature is 80 to 180 DEG C in reactor reaction for 2 to 24 hours; D natural cooling to room temperature after separation of B mixture, reaction after washing and drying. The preparation method of the invention is simple, and no strong acid, strong alkali and organic solvent are involved in the preparation process, and compared with other preparation methods, the utility model has the advantages of no environmental pollution and no need of calcination.
【技术实现步骤摘要】
本专利技术属于无机化工材料制备
，尤其是涉及一种主要用于在环境保护中处理污水的金纳米颗粒修饰氧化锌(ZnO)的制备方法。
技术介绍
当前，世界各国在享受经济高速增长的同时，也正面临着世界历史上规模最大、涉及面最广、后果最严重的环境污染问题。高度重视污水排放、废弃物等污染的处理和循环再生，减少资源的消耗和环境污染，走可持续发展道路已成为世界各国发展过程中共同面临的问题。中国在这方面所面临的挑战尤为严峻。近年来发展起来的以半导体金属氧化物为催化剂的光催化技术，为我们提供了一种理想的能源利用和治理环境污染的方法。重视和加强这方面的研究工作对各国经济的可持续发展、加强环境保护具有重要意义。氧化锌(ZnO)是一种直接带隙半导体，其室温下的禁带宽度为3.26￥，激子结合能为60meV，可以实现室温下的激子发射，产生近紫外的短波发光，被用来制备短波光电器件，如紫外探测器，紫外激光器等。另外氧化锌还具有很好的导电、导热和化学稳定性能，在太阳能电池、传感器和光催化等许多方面都有广泛的应用前景，因而成为国际上半导体材料研究领域的热点之一。近期的研究表明，在半导体表面负载金(A...
【技术保护点】
一种金纳米颗粒修饰氧化锌的制备方法，其特征在于它包括如下步骤：ａ、将锌盐溶液与六次甲基四胺溶液均匀搅拌，锌盐溶液与六次甲基四胺溶液物质的量的比例为１∶１～４；ｂ、在锌盐溶液与六次甲基四胺溶液组成的混合液Ａ中添加金盐溶液并均匀搅拌，金盐溶液与锌盐溶液物质的量的比例为１∶１００～１０００；ｃ、将锌盐溶液、六次甲基四胺溶液和金盐溶液组成的混合液Ｂ移到反应温度为８０～１８０℃的反应釜中反应２～２４小时；ｄ、自然冷却至常温后分离反应后的混合液Ｂ，洗涤，干燥。
【技术特征摘要】
【专利技术属性】
技术研发人员：徐建，吴立敏，辛立辉，朱丽娜，陈永康，何慈晖，
申请(专利权)人：上海市计量测试技术研究院，
类型：发明
国别省市：31[中国|上海]