For with ethylene, acetic acid and oxygen or oxygen-containing gas as raw material, preparation method of vinyl acetate in fixed bed gas phase reaction, the reaction temperature is 100 to 210 DEG C, the reactor entrance pressure is 0.5 ~ 2.0MPa. The catalyst carrier is SiO down 2 or SiO down 2 - Al: 2 O: 3 mixture of active components containing Pd and KOAc, the catalyst particles into a rod, cross section is the center of the impeller impeller shape, with a circular leaf number was 3 ~ 7. Particle length L is 3 ~ 6mm, the central hole of D1 diameter is 1 ~ 2.5mm, the impeller outer diameter of D2 is 3.5 ~ 8. The invention has the advantages that a suitable volume gas channel exists in the catalyst bed, not only has a high space-time yield and a low bed pressure drop loss, but also has excellent selectivity.
【技术实现步骤摘要】
本专利技术涉及以乙烯、醋酸及氧气或含氧气体为原料，气相反应制备醋酸乙烯酯的方法。以乙烯、醋酸及氧气或含氧气体为原料，在固定床反应器中气相反应制备醋酸乙烯酯已是较成熟的工艺，合适的催化剂是活性组份含有Pd和KOAc，并可含有Au、Ba或Cd，和/或其相应的盐类化合物，这些活性组份通常负载于SiO2或SiO2-Al2O3的混合物上。这类催化剂的活性组份早已趋于成熟，70年代以后人们较多的是对其活性组份在载体上的分布方式展开研究，并不断有蛋黄型、蛋白型及蛋壳型等活性组份呈非均匀分布的催化剂推出。活性组份非均匀分布的催化剂相对于均匀分布的催化剂来说，其表观活性、选择性和抗中毒能力均有明显的提高。上述传统的催化剂，不管活性组份是否呈均匀或非均匀分布，催化剂颗粒一般为球形，以后的研究结果发现，基于球形载体的催化剂在高空速反应条件下床层压降太大，给工艺操作带来了困难，而一些非球形的异形颗粒催化剂则能较好地适应高空速的操作条件。如专利EP 0464633A1便推出了多种用于气相反应制备醋酸乙烯酯的异形棒状催化剂，截面形状有“8”字形、“品”字形以及多孔圆等。与传统球形催化剂...
【技术保护点】
一种用于以乙烯、醋酸及氧气或含氧气体为原料，气相反应制备醋酸乙烯酯的方法，反应温度为１００～２１０℃，反应器入口压力为０．５～２．０ＭＰａ，进料原料的摩尔百分比为：乙烯∶醋酸∶氧＝（７５～８５）∶（１０～２０）∶（３～７），ＷＷＨ为（１６００～３０００）ｈｒ↑［－１］，反应原料混合气通过下述催化剂构成的固定床层进行反应制得醋酸乙烯酯，催化剂载体为ＳｉＯ↓［２］或者为ＳｉＯ↓［２］－Ａｌ↓［２］Ｏ↓［３］的混合物，负载的活性组份含有Ｐｄ和ＫＯＡｃ，活性组份为蛋壳型非均匀分布，其特征是催化剂颗粒为棒状，其截面呈叶轮状，叶轮中心有一园孔，叶为半园状，叶数目为３～７个，颗粒长度Ｌ为...
【技术特征摘要】
【专利技术属性】
技术研发人员：杨运信，王桢祺，
申请(专利权)人：中国石化上海石油化工股份有限公司，
类型：发明
国别省市：31[中国|上海]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。