一种焊接用锡材料的抗氧化保护剂制造技术

本发明专利技术提供一种焊接用锡材料的抗氧化保护剂，采用如下方法配制：首先将石蜡或含蜡物溶解于甲苯溶液中；然后，将上述溶液加入３０－５５倍重量的正己烷中混匀静置，备用。将该抗氧化保护剂，覆于锡球、粉末等锡制品表面，形成一层保护膜，使锡球、粉末等锡制品与空气隔绝，减少氧化机会，防止其表面被氧化。经过处理后的焊锡球、锡粉末，可在干燥大气中长期保存而不被氧化，并且其导电和焊接性能都不受影响，具有成本较低，容易制备等特点。

Antioxidant protective agent for tin material for welding

The invention provides a welding tin material protective agent, using the following method: firstly, preparation of paraffin or wax dissolved in toluene solution; then, n-hexane the solution to 30 to 55 times the weight of the mix static, standby. The antioxidant protective agent, coating on powder solder, tin products surface, forming a layer of protective film, solder balls and powder tin products isolated from the air, reduce oxygenation and prevent the surface oxidation. The treated solder ball and tin powder can be stored for a long time in the dry atmosphere without being oxidized, and the conductive and welding properties of the powder are not affected. The utility model has the characteristics of low cost and easy preparation.

【技术实现步骤摘要】

本专利技术涉及一种防止金属材料表面被氧化的保护剂，尤其是作为焊接用锡金属球、锡粉末等锡材料的抗氧化保护剂。
技术介绍
锡金属因熔点较低、导电性能好而作为理想的低温焊接材料，广泛运用在强电路、 芯片、集成电路板等电路连接上。但，正是由于其熔点较低，其抗氧化性能较弱，在空气中容 易被氧化，时间稍长在其表面就形成一层氧化膜层，表面逐渐变灰、变暗、发黑，甚至产生黑 点，使其失去金属光泽，进而影响其性能，如降低导电性能、降低焊接性能等。现有技术中的 焊接用锡材料，通常需要将锡金属加工成为细小的锡球或粉末，更加增大了其与空气的接 触面积，更容易被氧化。作为焊接用锡球、锡粉末等从生产厂家生产出来后，经过运输到达 零售商的仓库，再销售给终端用户使用，该过程通常要持续一段时间，短则十来天，长则一、 两年，随着时间的延长，锡球或粉末等被空气逐渐氧化，其氧化程度加剧，降低其多项性能 指标而不能作为焊接材料使用，甚至被迫报废。 本领域技术人员为此进行了大量的研究，例如CN101412112公开了一种用于焊 锡粉末防氧化的处理方法，该方法采用苯并三氮唑或羟基苯并三唑等有机物作为成膜物 质，并溶解到溶剂中，本文档来自技高网...

【技术保护点】
一种焊接用锡材料的抗氧化保护剂，其特征在于，采用如下步骤配制：　　首先，将石蜡或含蜡物质溶解于适量的甲苯溶液中；然后，将上述溶液加入３０－５５倍重量的正己烷中混匀静置，得到备用的焊接用锡材料的抗氧化保护剂。

【技术特征摘要】
一种焊接用锡材料的抗氧化保护剂，其特征在于，采用如下步骤配制首先，将石蜡或含蜡物质溶解于适量的甲苯溶液中；然后，将上述溶液加入30-55倍重量的正己烷中混匀静置，得到备用的焊接用锡材料的抗氧化保护剂。2. 根据权利要求1所述的焊接用锡材料的抗氧化保护剂，其特征在于...