Polyurethane cable shielding composite with special adhesive and manufacturing method is a polyurethane adhesive in organic chemical and manufacturing methods of each component added to the weight percentage of total amount respectively: 15.73 ~ 19.4% ethylene glycol adipic acid 32.6 ~ 31% benzene two formic acid 3.626 ~ 3.45% toluene diisocyanate 1.5 ~ 1.78% and 46.55 ~ 44.38% ethyl acetate method the manufacturing for the first mixture of ethylene glycol and adipic acid, then adding benzene two formic acid, and then produce polyester polycondensation, toluene diisocyanate added to produce main adhesive, finally adding adhesive diluted with ethyl acetate: cost method. The product is resistant to oil, water, high temperature and high adhesion.
【技术实现步骤摘要】
本专利技术是一种高分子有机化工中的聚氨酯粘合剂及其制造方法,特别是一种聚氨酯电缆屏蔽复合带专用粘合剂及其制造方法。电缆屏蔽铝塑复合带是由其挤膜、粘合剂、铝箔经干式复合加工而成,在电缆线内起屏蔽外界静电的作用,保证远距离通话声音高度清晰,因而是决定电缆质量的关键材料。而生产该复合带的主要原材料之一的粘合剂却一直没有达到理想的水平,如中国专利“ZL85100023”提出了一种聚氨酯粘合剂及其制造工艺,该粘合剂的特点是耐低温性能好,工艺性能好,适用于某些特殊的场合,但这种粘合剂的耐油、耐水的性能较差,不宜使用在电缆屏蔽复合带上。本专利技术的目的就是提供一种耐水、耐油、粘接力高的。本专利技术的粘合剂由己二酸、间苯二甲酸、乙二醇、甲苯二异氰酸酯、醋酸乙酯所组成,各成份的加入重量占总加入量的百分比分别为乙二醇 15.73~19.4%己二酸 32.6~31%间苯二甲酸 3.626~3.45%甲苯二异氰酸酯 1.5~1.78%醋酸乙酯 46.55~44.38%本专利技术的制造方法为①混合首先将乙二醇和己二酸混合,加温至210℃,保持24小时,然后加入间苯二甲酸在210℃的条件下保持6小时。②缩聚将以上混合后的液体在250℃的条件下减压至755毫米汞柱,即生成所需中间原料聚酯以及附产品醇和水。③加成将前步骤生成的聚酯加入甲苯二异氰酸酯在90~100℃的条件下生成主胶。④稀释最后加入醋酸乙酯即成本专利技术的产品。本专利技术中乙二醇的加入量在其允许的变化范围内一般取其较少量为宜,因为加大该成份,对最终的产品总量没有影响。本专利技术的优点在于粘接力高、耐水、 ...
【技术保护点】
一种聚氨酯电缆屏蔽复合带专用粘合剂,其特征在于该粘合剂由已二酸、间苯二甲酸、乙二醇、甲苯二异氰酸酯、醋酸乙酯所组成,各成份的加入重量占总加入量的百分比分别为:乙二醇 15.73~19.4%已二酸 32.6~31%间苯二甲酸 3. 626~3.45%甲苯二异氰酸酯 1.5~1.78%醋酸乙酯 46.55~44.38%。
【技术特征摘要】
1.一种聚氨酯电缆屏蔽复合带专用粘合剂,其特征在于该粘合剂由己二酸、间苯二甲酸、乙二醇、甲苯二异氰酸酯、醋酸乙酯所组成,各成份的加入重量占总加入量的百分比分别为乙二醇 15.73~19.4%己二酸 32.6~31%间苯二甲酸 3.626~3.45%甲苯二异氰酸酯 1.5~1.78%醋酸乙酯46.55~44.38%2.一种聚氨酯电缆屏蔽复合带专用粘...
【专利技术属性】
技术研发人员:蔡炳照,徐罗芬,
申请(专利权)人:金坛市胶粘剂厂,
类型:发明
国别省市:32[中国|江苏]