High temperature cooking bags polyurethane composite dry adhesive and manufacturing method is a kind of polyurethane adhesive and its manufacturing method, product components according to weight percentage of the group is divided into: two DEG 13.64 ~ 18.6% sebacic acid 23.26 ~ 25.73%1.2 propylene glycol 2.06 ~ 2.94% benzene two formic acid 6 ~ 5.43% two 3.86 ~ 5.74% acetic acid phenyl methane diisocyanate 48.71 ~ 44.03% ethyl manufacturing method is as follows: firstly the two glycol sebacic acid mixture, then add 1.2 propylene glycol and benzene two formic acid, then condensation, decompression to 755 mm Hg to generate polyester, then add two phenyl methane diisocyanate produce main adhesive, finally adding ethyl acetate dilution, completion of the invention.
【技术实现步骤摘要】
本专利技术是一种聚氨酯粘合剂及制造方法，尤其是用于高温蒸煮袋的干式复合粘合剂及其制造方法。当今世界上食品包装行业对直接将食品包装袋连同食品一道进行高温蒸煮的要求越来越高，使用高温蒸煮袋可直接将生产的食物加佐料后封于袋内加温至121℃以上进行蒸煮加工成熟食，简化了食品的生产工艺，保证了食品的卫生可靠性。由于蒸煮袋由塑膜与塑膜或塑膜/铝膜/塑膜的结合方式组成，塑膜与塑膜之间或塑膜或铝膜之间由耐蒸煮的粘合剂干式复合加工而成，具有优良的粘合性。而目前已有的粘合剂如中国专利“ZL87104917”名为无毒聚氨酯胶粘剂及其制备，该胶粘剂的最大问题是耐高温性能差，不能在高温蒸煮的情况下，保持高强的粘合性，因此对高温蒸煮包装袋并不适用。本专利技术的目的就是提供一种具有耐湿、耐高温的。本专利技术的聚氨酯高温蒸煮袋干式复合粘合剂按重量百分比的组份为二甘醇 13.64～18.6％癸二酸 23.26～25.73％1.2一丙二醇 2.06～2.94％间苯二甲酸 6～5.43％二苯基甲烷二异氰酸酯3.86～5.74％醋酸乙酯48.71～44.03％本专利技术的聚氨酯高温蒸煮袋干式复合粘合剂的制造方法为①混合将二甘醇和癸二酸混合加温220±2℃在氮气和胺类催化剂的作用下持续25小时，然后加入1.2一丙二醇和间苯二甲酸在200℃±2℃的条件下持续12小时。②缩聚将前道工序减压至755毫米汞柱，生成中间原料聚酯及废水、废醇。③加成将前道工序生成的聚酯加入二苯基甲烷二异氰酸酯升温至90～100℃生成主胶。④稀释将生成的主胶加入醋酸乙酯，升温至80～90℃制成粘合剂。本专利技术的优...
【技术保护点】
一种聚氨酯高温蒸煮袋干式复合粘合剂，由二甘醇、癸二酸、间苯二甲酸等所组成，其特征在于该粘合剂按重量百分比的组份为： 二甘醇 １３．６４～１８．６％ 癸二酸 ２３．２６～２５．７３％ １．２一丙二醇 ２．０６～２．９４％ 间苯二甲酸 ６～５．４３％ 二苯基甲烷二异氰酸酯 ３．８６～５．７４％ 醋酸乙酯 ４８．７１～４４．０３％。
【技术特征摘要】
1．一种聚氨酯高温蒸煮袋干式复合粘合剂，由二甘醇、癸二酸、间苯二甲酸等所组成，其特征在于该粘合剂按重量百分比的组份为二甘醇13.64～18.6％癸二酸23.26～25.73％1.2-丙二醇2.06～2.94％间苯二甲酸6～5.43％二苯基甲烷二异氰酸酯 3.86～5.74％醋酸乙酯 48.71～44.03％2．一种聚氨酯高温蒸煮袋干式复合粘合剂的制造方法，其特征在于...
【专利技术属性】
技术研发人员：蔡炳照，徐罗芬，
申请(专利权)人：金坛市胶粘剂厂，
类型：发明
国别省市：32[中国|江苏]
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。