The invention relates to the technical field of graphene preparation, in particular to a method for preparing graphene, which is characterized in that the expandable graphite is heated to 850 \u2103 - 900 \u2103 in a graphite expansion furnace, and then expands to obtain the expanded graphite with a gap of 0.7 \u2011 0.8nm. The expanded graphite contains a functional group containing hydroxyl and carboxyl groups with oxygen content of 2% \u2011 3%, and then the expanded graphite is dispersed in a strong polarity The method has the advantages of simple steps, high production efficiency, low production cost, complete structure, few layers, no stacking, no agglomeration and fewer defects.
【技术实现步骤摘要】
一种制备石墨烯的方法
本专利技术涉及石墨烯制备
，具体地说是一种步骤简单、生产效率高、生产成本低、得到的石墨烯具有结构完整、不回叠不团聚、缺陷较少的制备石墨烯的方法。
技术介绍
众所周知，石墨烯是一种半金属材料，其中碳原子通过二维sp2键合形成六角蜂巢晶格的单原子层状结构的材料，具有结构和化学稳定性以及非常优异的导电、导热以及机械性能，在能源、电子材料、生物医学以及环境保护等诸多领域具有潜在的应用前景。由于石墨烯的众多优点和优异的性能，已经提出和研究了大量生产石墨烯的方法。具体的，已经以各种方式研究了能够通过更简化的工艺制备具有较少缺陷且具有较少厚度的石墨烯的方法，使得石墨烯优异的性能可以更显著的表现。制备石墨烯的现有方法主要包括：微机械剥离法、氧化还原法、外延生长法、化学气相沉积法等。微机械剥离法最为简便，但只能得到数量极为少数的石墨烯。氧化还原法是目前应用较多的方法，主要是通过对石墨的氧化进行剥离以获得氧化石墨烯然后再还原得到石墨烯，此法在制备过程中会引入大量缺陷，在还原时不能完全修复，严重影响了其性能及应...
【技术保护点】
1.一种制备石墨烯的方法，其特征在于：取可膨胀石墨在石墨膨胀炉中升温至850℃-900℃后膨胀得到间隙为0.7-0.8nm的膨胀石墨，膨胀石墨中带有氧含量为2%-3%的含羟基和羧基的官能团，然后将得到的膨胀石墨分散于强极性溶剂中得石墨层间化合物，空化装置循环空化得石墨烯浆料。/n
【技术特征摘要】
1.一种制备石墨烯的方法，其特征在于：取可膨胀石墨在石墨膨胀炉中升温至850℃-900℃后膨胀得到间隙为0.7-0.8nm的膨胀石墨，膨胀石墨中带有氧含量为2%-3%的含羟基和羧基的官能团，然后将得到的膨胀石墨分散于强极性溶剂中得石墨层间化合物，空化装置循环空化得石墨烯浆料。
2.根据权利要求1所述的一种制备石墨烯的方法，其特征在于所述的可膨胀石墨倍率为100mL/g-700mL/g，优选300mL/g-500mL/g；纯度90%-99.99%，优先纯度95%-99.9%；粒径大小50-1200目，优选粒径80-325目，含氧量2%-5%，优选2%-3%。
3.根据权利要求1所述的一种制备石墨烯的方法，其特征在于所述的强极性溶剂是水、乙醇、甲酰胺、乙酰胺、氮甲基吡咯烷酮羧酸、四氢呋喃中的一种或几种的混合物...
【专利技术属性】
技术研发人员：费连东，程瑾宁，王政玉，姜圣，包彦彦，
申请(专利权)人：威海云山科技有限公司，
类型：发明
国别省市：山东;37