The invention relates to a metal ion doped WO3 aerochromic film and its preparation method and application. The preparation method of the metal ion doped WO3 aerochromic film includes the following steps: (1) dissolving tungsten hexachloride and nickel chloride hexahydrate in anhydrous ethanol to obtain a sol precursor; (2) coating the sol precursor on the substrate. (3) The doped film is irradiated under ultraviolet lamp to obtain the metal ion doped WO3 gas chromogenic film. The prepared metal ion doped WO3 gas chromogenic film can be applied to infrared control and high temperature gas chromogenic film. Compared with the prior art, the preparation process of the present invention is simple, fast, novel and unique, and has high stability, durability, high temperature resistance, strong cyclicity and enhanced near infrared absorption.
【技术实现步骤摘要】
一种金属离子掺杂WO3气致变色薄膜及其制备方法和应用
本专利技术属于气致变色
，尤其是涉及一种金属离子掺杂WO3气致变色薄膜及其制备方法和应用。
技术介绍
WO3薄膜具有优异的变色特性，是一种非常好的功能性材料，具有光致变色、热致变色、电致变色、气致变色等特性；气致变色结构简单，影响因素少，全为固态材料，而且其光学调节范围更广，易于大面积生产，因而具有更佳广阔的应用前景。传统三氧化钨薄膜处于致色态时，主要吸收峰在1000nm处，而太阳光的主要能量集中在近红外处，所以需要加大WO3气致变色薄膜在致色态时在近红外波段的吸收，从而具有更好的节能效果。
技术实现思路
本专利技术的目的就是为了克服上述现有技术存在的缺陷而提供一种金属离子掺杂WO3气致变色薄膜及其制备方法和应用。本专利技术的目的可以通过以下技术方案来实现：本专利技术提供一种金属离子掺杂WO3气致变色薄膜的制备方法，包括以下步骤：(1)将六氯化钨和六水合氯化镍溶解于无水乙醇中，得到溶胶前驱体；(2)将溶胶前驱体涂覆于基底上，形成掺杂薄膜；(3)将掺杂薄膜置于紫外灯下照射，得到所述的金属离子掺杂WO3气致变色薄...
【技术保护点】
1.一种金属离子掺杂WO3气致变色薄膜的制备方法，其特征在于，包括以下步骤：(1)将六氯化钨和六水合氯化镍溶解于无水乙醇中，得到溶胶前驱体；(2)将溶胶前驱体涂覆于基底上，形成掺杂薄膜；(3)将掺杂薄膜置于紫外灯下照射，得到所述的金属离子掺杂WO3气致变色薄膜。
【技术特征摘要】
1.一种金属离子掺杂WO3气致变色薄膜的制备方法，其特征在于，包括以下步骤：(1)将六氯化钨和六水合氯化镍溶解于无水乙醇中，得到溶胶前驱体；(2)将溶胶前驱体涂覆于基底上，形成掺杂薄膜；(3)将掺杂薄膜置于紫外灯下照射，得到所述的金属离子掺杂WO3气致变色薄膜。2.根据权利要求1所述的一种金属离子掺杂WO3气致变色薄膜的制备方法，其特征在于，所述的六氯化钨与六水合氯化镍的质量之比为4:1～8:1。3.根据权利要求1所述的一种金属离子掺杂WO3气致变色薄膜的制备方法，其特征在于，所述的无水乙醇与六氯化钨的摩尔比为100：3～400：3。4.根据权利要求1所述的一种金属离子掺杂WO3气致变色薄膜的制备方法，其特征在于，通过旋涂仪进...
【专利技术属性】
技术研发人员：高国华，祁万钰，吴广明，王浩然，朱琼，沈军，岑定成，于成龙，
申请(专利权)人：同济大学，
类型：发明
国别省市：上海,31
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。