The invention relates to a production system of glass fiber reinforced PBT material, which in turn comprises a glass fiber/PBT fiber blending device, a screw extruding device, a cooling device, a traction device and a granulating device. The screw extruding device comprises five heating zones, namely, the first heating zone, the second heating zone, the third heating zone, the fourth heating zone and the fifth heating zone. The fourth heating zone is provided with a filler adding device. The overall tension strength of the invention is obviously increased, and the warpage of the product is obviously improved.
【技术实现步骤摘要】
一种玻纤增强PBT材料的生产系统
本专利技术属于增强PBT纤维的
,具体涉及一种玻纤增强PBT纤维的生产系统。
技术介绍
聚对苯二甲酸丁二酯(PBT)是优良的热塑性材料,有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性,但PBT吸湿特性很弱,张力强度一般,仅为50MPa,PBT的结晶很迅速,这将导致因冷却不均匀而造成弯曲变形。
技术实现思路
专利技术目的:本专利技术的目的是为了克服现有技术中的不足,提供一种整体张力强度明显增大,制品翘曲性得到明显改善的玻纤增强PBT材料的生产系统。技术方案:为了解决上述技术问题,本专利技术所述的一种玻纤增强PBT材料的生产系统,它依次包括玻纤/PBT纤维共混装置、螺杆挤压装置、冷却装置、牵引装置和切粒装置,所述螺杆挤压装置包括五段加热区,分别为第一加热区、第二加热区、第三加热区、第四加热区和第五加热区,在所述螺杆挤压装置的第四加热区处设有填料添加装置。所述玻纤/PBT纤维共混装置为高速混合机。所述螺杆挤压装置为一体化分区加热式螺杆熔融装置。所述填料添加装置为纵横尺寸相近填料添加装置。有益效果:本专利技术与现有技术相比,其显著优点是:本专利技术整体结构设置合理,采用玻纤/PBT纤维共混装置,加入玻璃纤维增强,使整体张力强度明显增大,可达170MPa,采用纵横尺寸相近填料添加装置,在共混体中再加入纵横尺寸相近的填料,使整体在流程的垂直方向张力强度明显改善,制品的翘曲性得到很好改善,这更有利于制备各类精密制件,所得产品性能好、价格适中,使用寿命长。附图说明图1是本专利技术的整体连接示意图;图2是本专利技术中所述螺杆挤压装置 ...
【技术保护点】
1.一种玻纤增强PBT材料的生产系统,其特征在于:它依次包括玻纤/PBT纤维共混装置(1)、螺杆挤压装置(2)、冷却装置(3)、牵引装置(4)和切粒装置(5),所述螺杆挤压装置(2)包括五段加热区,分别为第一加热区(6)、第二加热区(7)、第三加热区(8)、第四加热区(9)和第五加热区(10),在所述螺杆挤压装置(2)的第四加热区(9)处设有填料添加装置(11)。
【技术特征摘要】
1.一种玻纤增强PBT材料的生产系统,其特征在于:它依次包括玻纤/PBT纤维共混装置(1)、螺杆挤压装置(2)、冷却装置(3)、牵引装置(4)和切粒装置(5),所述螺杆挤压装置(2)包括五段加热区,分别为第一加热区(6)、第二加热区(7)、第三加热区(8)、第四加热区(9)和第五加热区(10),在所述螺杆挤压装置(2)的第四加热区(9)处设有填料添加装置(...
【专利技术属性】
技术研发人员:俞盛,李建民,
申请(专利权)人:无锡市兴盛新材料科技有限公司,
类型:发明
国别省市:江苏,32