The invention relates to the field of LED lighting, in which the glare generated by the luminescence of atomized LED chips reduces the damage to the retina. Modified plastics for manufacturing lamp tubes and lampshades. It is characterized by optical grade polypropylene plastics with particle size less than 5 microns. The purity of holmium oxide is more than 99.5% and its particle size is less than 50 nanometers. The weight ratio is 2%-9%. The purity of barium sulfate is over 98%, the particle size is less than 80 nanometers, and the weight ratio is 3%11%. After shaping, nano-holmium oxide and nano-barium sulfate are formed inside the plastic, which can effectively improve the glare emitted by the LED chip and reduce the damage to the retina and uncomfortable feeling.
【技术实现步骤摘要】
一种LED灯管的改性塑料制备方法
本专利技术涉及LED照明领域，雾化由LED芯片发光产生的眩光，降低对视网膜的伤害，用于制造灯管及灯罩的改性塑料。
技术介绍
LED芯片制造的灯具是环保、节能的环境友好型灯具，由于LED芯片工作在450-480纳米波段，所产生的光谱，在其光谱上覆有荧光剂。从而激发转为白光，在白光中会产生一部分眩光，对人体视网膜有伤害。
技术实现思路
本专利技术减少LED芯片工作时产生的眩光，使之透过灯管及灯罩产生的柔和光线，减少对人体及视网膜的不舒服的感觉。为改善LED芯片产生的眩光缺陷，以添加雾化光谱的物质对光学塑料进行改性，使其保持高透光性，同时消除LED芯片工作时产生的眩光及不利光谱。本专利技术在于提供一种纳米硫酸钡和纳米氧化钬与光学塑料复合材料的制备方法。具体实施方式以下描述用于揭露本专利技术以使本领域技术人员能够实现本专利技术。以下描述中的优选实施例只作为举例，本领域技术人员可以想到其他显而易见的变型。本专利技术解决上述技术问题的技术方案是，将硫酸钡和氧化钬制备至纳米级，由于将上述二物质制备至纳米级后，比表面积大，活化度高，雾化度好，添加量少，不但不破坏原光学塑料粒子基本力学性能，还能将其提高钢性及耐温性。其特征在于光学级聚丙烯塑料，粒径≤5微米。纯度达99.5％以上氧化钬粒径≤50纳米，添加量，重量比为2％-9％。纯度达98％以上的硫酸钡，粒径≤80纳米，添加量，重量比为3％-11％，按需要解决眩光强度的要求，选定适合的物料比，采用共混方法，共同投入振动混料机内，在转速≤500转/分，运转时间≤150分钟。用以上改性塑料，在挤出机挤...
【技术保护点】
1.一种LED灯管的改性塑料，其特征在于光学级聚丙烯塑料，粒径≤5微米。纯度达99.5％以上氧化钬粒径≤50纳米，添加量，重量比为2％‑9％。纯度达98％以上的硫酸钡，粒径≤80纳米，添加量，重量比为3％‑11％。
【技术特征摘要】
1.一种LED灯管的改性塑料，其特征在于光学级聚丙烯塑料，粒径≤5微米。纯度达99.5％以上氧化钬粒径≤5...
【专利技术属性】
技术研发人员：黄维，
申请(专利权)人：宁波格尔登轨道交通科技有限公司，
类型：发明
国别省市：浙江,33