The hydrothermal preparation method of FeSmO3 nanometer powder relates to the preparation of a composite oxide material FeSmO3. Samarium acetate and ammonium ferric oxalate are used as raw materials to prepare FeSmO 3 and FeSmO 3 approximate spherical particles at low temperature by hydrothermal method. The average grain size of FeSmO 3 is 20 to 30 nm, and it has excellent visible photocatalytic activity. The invention develops a new industry for the preparation of FeSmO3 nano-powder products, and achieves the purposes of simple operation, fast and efficient, low energy consumption and industrialized production of FeSmO3 nano-powder.
【技术实现步骤摘要】
FeSmO3纳米粉体的水热制备方法
本专利技术涉及一种复合氧化物材料的制备，特别是涉及一种FeSmO3纳米粉体的水热制备方法。
技术介绍
FeSmO3是一种具有优异磁性能的永磁材料，正如文献(稀有金属，2007，31(3)：316-319)报道以Sm2O3和Fe(NO3)3为主要原料，采用共沉淀法经一系列反应过程制备得到沉淀物，将沉淀物于800℃至1000℃煅烧2h得到FeSmO3；文献(材料热处理学报，2005，26(4)：22-24)也报道以Sm2O3、HNO3和Fe(NO3)3为主要原料，采用溶胶-凝胶法经一系列反应过程制备得到干凝胶，将干凝胶于450℃煅烧5h，然后再升温至600℃煅烧1h得到FeSmO3。共沉淀法和溶胶-凝胶法都需高温煅烧过程，存在制备工艺较复杂、耗时长和能耗高等缺点，工业化应用前景堪忧。水热法通常是指在密闭反应器(如反应釜)中，采用水作为反应体系，通过对反应体系加热，创造一个相对高温、高压的反应环境，使通常难溶或不溶的物质溶解并且反应或重结晶，从而合成产品的一种方法。水热法制备的纳米产品通常具有粉末细、纯度高、分散性好、分布窄、晶型好，...
【技术保护点】
1.FeSmO3纳米粉体的水热制备方法，其特征在于包括以下步骤(1)在室温条件下，将0.006mol乙酸钐溶于40毫升60％的乙醇溶液得到A溶液，将0.004mol草酸铁铵溶于50ml蒸馏水中得到B溶液；(2)在搅拌条件下，将一定量的A溶液缓慢加入到B溶液中，持续搅拌10min，得到反应液；(3)将80毫升反应液转移至100毫升高压反应釜中，将反应釜放入一定温度的烘箱中恒温反应12h；(4)待反应釜自然冷却至室温，取出产品洗涤3次，将产品于80℃烘干得到FeSmO3纳米粉体样品。
【技术特征摘要】
1.FeSmO3纳米粉体的水热制备方法，其特征在于包括以下步骤(1)在室温条件下，将0.006mol乙酸钐溶于40毫升60％的乙醇溶液得到A溶液，将0.004mol草酸铁铵溶于50ml蒸馏水中得到B溶液；(2)在搅拌条件下，将一定量的A溶液缓慢加入到B溶液中，持续搅拌10min，得到反应液；(3)将80毫升反应液转移至100毫升高压反应釜中，将反应釜放入一定温度的烘箱中恒温反...
【专利技术属性】
技术研发人员：唐培松，陈海锋，王永亚，丁杨彬，吕春燕，
申请(专利权)人：湖州师范学院，
类型：发明
国别省市：浙江,33