The invention discloses a preparation method of beta FeOOH micron/submicron spheres. FeCl3 is placed in double-steaming water with iron trichloride and water as raw materials, dissolved by magnetic stirring to form a uniform solution, then the solution is placed in an open container, the water bath is heated and stirred and refluxed at the same time. After the reaction is completed, the obtained suspension is centrifuged and washed with double-steaming water and dried, and the average diameter is about 0. 6_2.0 um beta_FeOOH micron/submicron spheres. The raw material of the invention is only iron trichloride and water, with wide sources, low price, environmental protection, simple preparation method and process flow, simple operation, low requirement for equipment for atmospheric pressure reaction, safe operation, easy control of process, short production cycle, uniform product distribution, high yield, and is suitable for industrial production.
【技术实现步骤摘要】
一种β-FeOOH微米/亚微米球的制备方法
本专利技术属于无机非金属微米/亚微米材料制备
，具体涉及一种β-FeOOH微米/亚微米球的制备方法。
技术介绍
β-FeOOH又称为四方纤铁矿，橙黄色固体，作为铁元素的一种氧化物存在于自然界中，因具有无毒性、高分散性、化学稳定性好、比表面积大、着色能力强、良好的光催化性能和光稳定性等特性，在许多领域均有广泛应用，尤其是在污水处理方面。FeOOH可以有效地吸附污水中的重金属离子和有机染料等污染源。此外，β-FeOOH是制备α-Fe2O3、γ-Fe2O3、Fe3O4等材料重要的前驱体，且β-FeOOH微米/亚微米球在电池领域的应用十分广泛，尤其是在提高电容性能方面。因此，近年来β-FeOOH微米/亚微米球的制备成为了许多国内外研究者关注的热点。目前，β-FeOOH的制备方法有很多，例如：强迫水解法、沉淀法、亚铁氧化法、水热法、微乳液法、溶胶凝胶法、微波水解法等。利用这些方法可以制备出不同形状的FeOOH粒子，但是有些方法需要向系统中加入沉淀剂、表面活性剂、调整剂和稳定剂等物质，或者需要用到严苛的制备条件和复杂的仪器，且...
【技术保护点】
1.一种β‑FeOOH微米/亚微米球的制备方法，其特征在于，包括如下步骤：(1)将三氯化铁置于水中，磁力搅拌溶解形成均匀的三氯化铁溶液；(2)将溶液置于敞口容器内，水浴加热同时搅拌回流；(3)反应结束后，将得到的悬浮液离心并用水洗涤后干燥，得β‑FeOOH微米/亚微米球。
【技术特征摘要】
1.一种β-FeOOH微米/亚微米球的制备方法，其特征在于，包括如下步骤：(1)将三氯化铁置于水中，磁力搅拌溶解形成均匀的三氯化铁溶液；(2)将溶液置于敞口容器内，水浴加热同时搅拌回流；(3)反应结束后，将得到的悬浮液离心并用水洗涤后干燥，得β-FeOOH微米/亚微米球。2.根据权利要求1所述的制备方法，其特征在于，步骤(1)中所述的三氯化铁溶液浓度为0....