The invention belongs to the technical field of hydrophobic treatment of glass surface, in particular to a high transparent glass hydrophobic agent and a preparation method thereof. A high transparent glass hydrophobic agent is prepared by weight from 100 parts of dimethylcyclosiloxane, 20-50 parts of phenylsiloxane, 5-10 parts of silane coupling agent, 0.1-1 part of alkaline catalyst, 5-100 parts of non-ionic surfactant and 10-90 parts of solvent. It can form a transparent hydrophobic film on the glass surface, and water droplets form beads on the glass surface. The antenna reaches 110 degrees, which greatly speeds up the drop speed of water droplets, realizes automatic rolling without leaving traces, thus solving the problem of blurred vision.
【技术实现步骤摘要】
一种高透光玻璃疏水剂及其制备方法
本专利技术属于玻璃表面疏水处理
，特别涉及一种高透光玻璃疏水剂及其制备方法。
技术介绍
普通玻璃表面为亲水表面，水滴在玻璃上扩展时会使玻璃的透光性变差，而汽车挡风玻璃、侧挡风玻璃及前后视镜的模糊，是导致交通事故的重要原因。在下雨或高湿度的情况下汽车玻璃表面便会形成附着的液滴影响视线。市场上存在日常汽车保养用玻璃疏水剂，但其一般为短效疏水剂，抗沙尘侵蚀能力较弱，且使用时需要对玻璃表面进行清理才能达到叫好的疏水效果，使用条件较为苛刻，应用范围有限。
技术实现思路
本专利技术为了解决上述问题，提供一种高透光玻璃疏水剂，可以在玻璃表面形成一层透明的憎水膜，水滴在玻璃表面形成水珠，接触角高达110°，极大地加快了水滴的掉落速度，可实现自动滚落而不留痕迹，从而解决了视线不清的问题，并提供其制备方法。本专利技术采用以下技术方案来实现：一种高透光玻璃疏水剂，按重量份计，由如下原料制备而成：二甲基环体硅氧烷100份，含苯基硅氧烷20～50份，硅烷偶联剂5～10份，碱性催化剂0.1～1份，非离子表面活性剂5～100份，溶剂10～90份。优选的方案，...
【技术保护点】
1.一种高透光玻璃疏水剂，其特征在于，按重量份计，由如下原料制备而成：二甲基环体硅氧烷100份，含苯基硅氧烷20～50份，硅烷偶联剂5～10份，碱性催化剂0.1～1份，非离子表面活性剂5～100份，溶剂10～90份。
【技术特征摘要】
1.一种高透光玻璃疏水剂，其特征在于，按重量份计，由如下原料制备而成：二甲基环体硅氧烷100份，含苯基硅氧烷20～50份，硅烷偶联剂5～10份，碱性催化剂0.1～1份，非离子表面活性剂5～100份，溶剂10～90份。2.根据权利要求1所述的高透光玻璃疏水剂，其特征在于：所述二甲基环体硅氧烷包括八甲基环四硅氧烷、二甲基环硅氧烷中的一种或几种。3.根据权利要求1所述的高透光玻璃疏水剂，其特征在于：所述含苯基硅氧烷包括八苯基环四硅氧烷、四甲基四苯基环四硅氧烷、短链二甲基二苯基硅氧烷、短链甲基苯基硅氧烷中的一种或几种。4.根据权利要求1所述的高透光玻璃疏水剂，其特征在于：所述硅烷偶联剂为N-β-(氨乙基)-γ-氨丙基甲基三甲氧基硅烷。5.根据权利要求1所述的高透光玻璃疏水剂，其特征在于：所述碱性催化剂为四甲基氢氧化铵。6.根据权利要求1所述的高透光玻璃疏水剂，其特征在于...
【专利技术属性】
技术研发人员：王薛成，耿学辉，杨帆，杨开柱，
申请(专利权)人：湖北新四海化工股份有限公司，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。