The invention discloses a preparation method of nitrogen-doped mesoporous carbon carrier, which comprises the following steps: A. dissolving 2 g sucrose in 100 mL deionized water, stirring and dissolving, and adding 20 g melamine after complete dissolution. B. Put the above mixed solution in a water bath at 50 C, stir and steam, and then move it into a 50 C oven to dry overnight. C. The obtained solid is grinded and roasted in nitrogen atmosphere. The heating procedure is as follows: heating up to 350 C for 2 hours, then heating up to 800 C and then lowering to room temperature. The heating rate is 5 C/min, that is to say, the nitrogen-doped mesoporous carbon carrier is obtained. The invention uses melamine as N source and sucrose as C source to prepare nitrogen-doped mesoporous carbon carrier, which can load different metal particles and can be used to prepare corresponding catalysts.
【技术实现步骤摘要】
一种掺氮介孔碳载体的制备方法
本专利技术涉及催化剂载体
，公开了一种掺氮介孔碳载体的制备方法。
技术介绍
多孔材料相对连续介质材料而言，一般具有相对密度低、比强度高、比表面积高、重量轻、隔音、隔热、渗透性好等优点。国际纯粹与应用化学联合会(IUPAC)将多孔材料按它们孔直径的大小将其分为三类：微孔材料(microporousmaterials)孔径小于2nm；介孔材料(mesoporousmaterials)孔径在2-50nm；大孔材料(macroporousmaterials)孔径大于50nm。介孔材料具有极高的比表面积、规则有序的孔道结构、狭窄的孔径分布、孔径大小连续可调等特点，使得它在很多微孔沸石分子筛难以完成的大分子的吸附、分离，尤其是催化反应中发挥作用。与纯介孔硅材料相比，介孔碳材料表现出特殊的性质，有高的比表面积，高孔隙率；孔径尺寸在一定范围内可调；介孔形状多样，孔壁组成、结构和性质可调；通过优化合成条件可以得到高热稳定性和水热稳定性；合成简单、易操作、无生理毒性。为了进一步改善介孔孔碳材料在这些方面的应用，通常将杂原子(例如N、B、S等)或含杂...
【技术保护点】
1.一种掺氮介孔碳载体的制备方法，其特征在于具有以下的制备过程和步骤：A、称取2g蔗糖溶于100mL去离子水中搅拌溶解，完全溶解后加入20g三聚氰胺。B、将上述混合悬浊液置于50℃水浴锅中搅拌蒸干后移入50℃烘箱中干燥过夜。C、将得到的固体研磨后在氮气气氛下在管式炉中焙烧，升温程序为：升温至350℃保温2h，再升温至800℃后降至室温，升温速率为5℃/min，即得到掺氮介孔碳载体。
【技术特征摘要】
1.一种掺氮介孔碳载体的制备方法，其特征在于具有以下的制备过程和步骤：A、称取2g蔗糖溶于100mL去离子水中搅拌溶解，完全溶解后加入20g三聚氰胺。B、将上述混合悬浊液置于50℃水浴锅中搅拌蒸干后移入50℃烘箱中干燥过夜。C、将得到的固体研磨后在氮气气氛下在管式炉中焙烧，升温程序为：升温至350℃保温2h，再升温至800℃后降至室温，升温速率为5℃/min，即得到掺氮介孔碳载体。2.根据...
【专利技术属性】