The preparation method of a rubber silica composite belongs to the field of material preparation, and its characteristics include the following steps: mixing the composite materials in the order of EPDM stearic acid, zinc oxide, accelerator silica EEUG, KH 550, EPDM g MMH and silica mixture by using a torque rheometer, adding sulphur to the open rubber mixer and thinning through. Six times later, the blend was cured on the plate vulcanizer after parking overnight, and the preparation was completed. EEUG, KH_550 and EPDM_g_MMH can reduce the delayed vulcanization effect caused by silica, reduce the aggregation of silica and improve its dispersibility. With the increase of EEUG dosage, the tensile strength, tear strength, elongation at break and wear resistance of vulcanizates increase significantly.
【技术实现步骤摘要】
一种橡胶白炭黑复合材料的制备方法
本专利技术属于材料制备领域，尤其涉及一种橡胶白炭黑复合材料的制备方法。
技术介绍
三元乙丙橡胶(EPDM)是由乙烯、丙烯及非共轭二烯聚合产生的共聚物，由于其具有优良的耐热性、耐寒性、耐腐蚀性及高延展性等特点，其应用领域十分广泛，继丁苯橡胶(SBR)和顺丁橡胶(BR)之后成为世界第三大合成橡胶。近年来汽车用传动橡胶制品多楔带被广泛应用，而随着汽车工业的升级，多楔带的工作环境温度越来越高，传动带中常用的氯丁橡胶(CR)越来越难以满足耐高温的要求，而耐热性能优异的氢化丁腈橡胶(HNBR)和氟橡胶(FKM)价格过于昂贵，因此，耐热性能良好且较廉价的EPDM被广泛用于汽车用多楔带的主体材料。由于EPDM耐磨性、耐撕裂性及动态疲劳性能不佳，用于多楔带制品时需与其它材料并用进行改性。炭黑和白炭黑是橡胶工业中最主要的两类补强剂，白炭黑由于具有更小的粒径和更大的表面积，因此其补强的硫化胶拉伸强度、撕裂强度和耐磨性较高。但由于白炭黑表面含有大量的硅羟基，与非极性的橡胶相容性较差，大量填充时难以分散导致补强效果不理想，引起胶料加工性能、物理机械性能及动...
【技术保护点】
1.一种橡胶白炭黑复合材料的制备方法，其特征在于包括如下步骤：利用转矩流变仪将复合材料按照EPDM‑硬脂酸、氧化锌、促进剂‑白炭黑‑EEUG、KH‑550、EPDM‑g‑MMH和白炭黑混合物的加料顺序混炼均匀后，在开放式炼胶机中加入硫磺混炼，薄通６次后下片，混炼胶停放过夜后，将混炼胶在平板硫化机上硫化成型，完成制备。
【技术特征摘要】
1.一种橡胶白炭黑复合材料的制备方法，其特征在于包括如下步骤：利用转矩流变仪将复合材料按照EPDM-硬脂酸、氧化锌、促进剂-白炭黑-EEUG、KH-550、EPDM-g-MMH和白炭黑混合物的加料顺序混炼均匀后，在开放式炼胶机中加入硫磺混炼，薄通６次后下片，混炼胶停放过夜后，将混炼胶在平板硫化机上硫化成型，完成制备。2.根据权利要求1所述橡胶白炭黑复合材料的制备方法，其特征在于：所述复合材料的质量份配比为：EPDM100，白炭黑35-40，ZnO4.5-5，SA1-1.5，促进剂BZ1-1.5，促进剂PZ0.3-0.5，促进剂M0.3-0.5，促进剂TM...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。